镁合金带内筋筒形件热强旋成形质量及参数优化  

Forming Quality and Parameters Optimization for Hot Power Spinning of Magnesium Alloy Cylindrical Parts with Inner Ribs

作　　者：夏琴香[1] 江鹏 肖刚锋[1] 程秀全[2] 龙锦川 XIA Qin-xiang;JIANG Peng;XIAO Gang-feng;CHENG Xiu-quan;LONG Jin-chuan(School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,China;Department of Aircraft Maintenance Engineering,Guangzhou Civil Aviation College,Guangzhou 510403,China)

机构地区：[1]华南理工大学机械与汽车工程学院,广州510640 [2]广州民航职业技术学院飞机维修工程学院,广州510403

出　　处：《精密成形工程》2022年第5期1-7,共7页Journal of Netshape Forming Engineering

基　　金：国家自然科学基金(51775194)。

摘　　要：目的探明镁合金带内筋筒形件热强旋成形质量影响因素间的相互作用,并获得优化后的内筋数量及工艺参数。方法设计了五因素、三水平正交试验方案,开展了灰色关联度分析及极差分析,研究了内筋数量及工艺参数对旋压件直线度、圆度、筋背凹陷率、内筋饱和度、筋高不均匀度等成形质量指标影响的主次顺序,获得了最优的参数组合。结果各参数对旋压件成形质量的综合影响主次顺序为:内筋个数N>管坯壁厚t_(0)>减薄率ψ_(t)>成形温度T>进给比f,最优的参数组合为N=12、t_(0)=8 mm、ψ_(t)=70%、T=350℃、f=0.4 mm/r。结论通过在最优的参数组合下开展热强旋试验,可制备出质量合格的镁合金带内筋筒形件。This work aims to explore the interaction among influence factors of forming quality for hot power spinning of magnesium alloy cylindrical parts with inner ribs(CPIRs),and obtain the optimized inner rib number and processing parameters.A five-factor,three-level orthogonal test scheme was designed,the grey correlation analysis and range analysis were conducted,the influence of inner rib number and processing parameters on the forming quality indexes,such as straightness,roundness,concave ratio of the back of rib,saturation degree of inner ribs and inhomogeneity degree of inner ribs,the optimal parameter combination was obtained.The results show that the primary and secondary order of the comprehensive influence of various parameters on the forming quality of spun workpiece is:number of inner ribs N>wall thickness of cylindrical blank t_(0)>thinning rate of wall thicknessψ_(t)>forming temperature T>roller feed rate f,and the optimal parameters combination is:N=12,t_(0)=8 mm,ψ_(t)=70%,T=350℃,f=0.4 mm/r.Under the optimal parameters combination,the magnesium alloy CPIRs with qualified forming quality can be prepared by hot power spinning.

关 键 词：ZK61镁合金 带内筋筒形件 正交试验 热强旋 灰色关联度 

分 类 号：TG306[金属学及工艺—金属压力加工]