制备条件对球形氧化铝载体性质的影响  

Effect of preparation condition on the properties of spherical Alumina Carrier

作　　者：李慧胜 徐景东 艾子龙 Li Huisheng;Xu Jingdong;Ai Zilong(Sinochem Quanzhou Petrochemical Co.,Ltd.,Quanzhou362103,Fujian,China;Sinochem Quanzhou Energy Technology Co.,Ltd.,Quanzhou 362000,Fujian,China)

机构地区：[1]中化泉州石化有限公司,福建泉州362103 [2]中化泉州能源科技有限责任公司,福建泉州362000

出　　处：《工业催化》2022年第3期49-52,共4页Industrial Catalysis

摘　　要：通过调变合成条件,制备多种不同孔结构和机械强度的球形氧化铝载体。结果表明,随着酸含量的增加,载体的吸水率不断下降,机械强度先增大后减小,适宜的酸质量分数为2.5%;提高水粉质量比可使载体的吸水率提高,而强度先增大后减小,水粉质量比控制1.3为宜;两种原料混合可制备出性能更佳的球形氧化铝载体;适当提高载体的焙烧温度可扩大载体的孔径。A variety of spherical alumina carriers with different pore structure and mechanical strength were prepared by adjusting the synthesis condition.The results showed that with the increase of acid content,water absorption of the carrier decreased,the mechanical strength increased first and then decreased with acid content,and the appropriate acid content was 2.5%.Water absorption of the carrier could be increased by increasing water/powder ratio,while the strength increased first and then decreased with water/powder ratio,and the appropriate water/powder ratio was 1.3.The spherical alumina carrier with better performance could be prepared bymixing the two materials.Appropriately increasing calcination temperature of the carrier could enlarge its pore size.

关 键 词：催化剂工程 上流式反应器 球形氧化铝 孔结构 吸水率 机械强度 

分 类 号：TQ426.65[化学工程] TE624.43[石油与天然气工程—油气加工工程]