基于率相关三维弹塑性损伤模型的复合材料渐进失效分析  

Progressive failure analysis of composite materials based on rate-dependent three-dimensional elastoplastic damage model

作　　者：刘志明 陈静芬 毛欢 陈君昱 LIU Zhiming;CHEN Jingfen;MAO Huan;CHEN Junyu(MOE Key Laboratory of Disaster Forecast and Control in Engineering,School of Mechanics and Construction Engineering,Jinan University,Guangzhou 510632,China)

机构地区：[1]暨南大学力学与建筑工程学院“重大工程灾害与控制”教育部重点实验室,广州510632

出　　处：《复合材料学报》2022年第5期2482-2494,共13页Acta Materiae Compositae Sinica

基　　金：广东省自然科学基金面上项目(2021A1515010297)。

摘　　要：建立了一个同时考虑复合材料非线性力学响应、应变率效应和损伤累积导致材料属性退化的弹塑性三维损伤本构模型。采用改进的塑性力学模型表征材料在动态荷载下的非线性力学行为。为准确预测复合材料在动态荷载下的弹塑性力学响应,引入了率相关放大系数对准静态下的塑性强化函数进行修正。采用“断裂带模型”对已开发的本构模型软化段进行规则化,以减轻有限元分析结果的网格敏感性。采用分区反抛物线插值法对基体损伤初始断裂面角度及纤维扭结/劈裂平面角度进行求解。开发包含数值积分算法的用户材料自定义子程序VUMAT,并嵌于有限元程序ABAQUS V6.14中,对力学行为展现显著非线性力学效应和应变率效应的IM7/8552碳纤维/环氧树脂复合材料层合板进行了渐进失效分析,验证本文提出的材料本构模型的有效性。结果显示,预测结果与已报道的试验结果吻合良好,表明已建立的率相关三维弹塑性损伤本构模型能准确预测此类复合材料层合板的在动态荷载下的力学行为,为复合材料构件及其结构设计提供了一种有效的分析方法。A three-dimensional elastoplastic damage constitutive model which takes into account the nonlinear mechanical response,strain rate effects of composites,material properties degradation due to damage evolution was proposed.A modified plastic model was used to characterize the nonlinear mechanical response under dynamic load.To accurately describe the elastoplastic mechanical response of composite materials under dynamic load,the rate-dependent amplification factor was introduced to modify the plastic hardening law under static condition.In order to alleviate mesh sensitivity of finite element analysis results,the“Crack Band Theory”was applied to regularize the softening branch of the material constitutive model.The Selective Range Inverse Parabolic Interpolation algorithm was used to calculate the angle of the initial fracture plane of matrix damage and the angle of the fiber kinking/splitting plane.User-defined material subroutine VUMAT containing the numerical integration algorithm was coded and implemented in finite element procedure ABAQUS V6.14.The efficiency of the material constitutive model was demonstrated through progressive failure analysis of IM7/8552 carbon fiber/epoxy composite laminates,the mechanical behavior of which demonstrates significant nonlinear mechanical response.The numerical results agree well with the experimental data reported in the literature.It is shown that the rate-dependent three-dimensional elastoplastic damage constitutive model can predict the mechanical behavior of composites under dynamic loads with sufficient accuracy.The proposed approach provides an efficient method for the design of composite components and structures.

关 键 词：复合材料 应变率效应 塑性效应 三维损伤本构模型 渐进失效分析 