一步法制备Janus中空纤维膜及其膜蒸馏性能研究  

Preparation of Janus hollow fiber membrane via one-step strategy and study on its membrane distillation performance

作　　者：李明[1,2] 孙扬 王聪 康国栋 付晓燕[3] 于海军 曹义鸣[1] 金焱[4] LI Ming;SUN Yang;WANG Cong;KANG Guodong;FU Xiaoyan;YU Haijun;CAO Yiming;JIN Yan(Dalian Institute of Chemical Physics(DICP),Chinese Academy of Sciences(CAS),Dalian 116023,China;University of Chinese Academy of Sciences,Beijing 100049,China;Dalian Ecological Environment Monitoring Center of Liaoning Province,Dalian 116023,China;Vontron Technology Co.,Ltd.Guiyang 550014,China)

机构地区：[1]中国科学院大连化学物理研究所,大连116023 [2]中国科学院大学,北京100049 [3]辽宁省大连生态环境监测中心,大连116023 [4]沃顿科技股份有限公司,贵阳550014

出　　处：《膜科学与技术》2022年第3期32-40,共9页Membrane Science and Technology

基　　金：国家自然科学基金面上项目(22178334);中国科学院洁净能源创新研究院合作基金(DNL201909);辽宁省自然科学基金(2019-MS-313);大连市科技创新基金应用基础研究项目(2019J12SN67)。

摘　　要：利用亲水改性材料与聚偏氟乙烯共混配制铸膜液,通过正丙醇水两次凝胶调控相转化过程,促进亲水性聚合物向中空纤维内表面偏析,从而改变了膜两侧亲疏水性结构,制备出具有非对称浸润性的Janus中空纤维膜,考察亲水性聚合物添加量等因素对膜性能的影响.所制备的Janus中空纤维膜外侧水接触角超过135°,内侧水接触角约为55°.在原料液温度60℃、渗透液温度10℃情况下,直接接触式膜蒸馏(DCMD)过程渗透通量约为35kg/(m^(2)·h).200 min连续实验中盐截留率始终保持在98%以上.The hydrophilic material is blended with polyvinylidene fluoride to prepare the membrane casting solution.By regulating the phase inversion process,promoting the segregation of hydrophilic polymer to the inner surface,changing the structure of both sides of the hollow fiber membrane,the Janus hollow fiber membrane with asymmetric wettability was prepared,and the influence of the concentration of hydrophilic material added in the membrane casting solution was explored.The prepared Janus hollow fiber membrane has an outer side water contact angle of more than 135°,and an inner side water contact angle of about 55°.When the temperature of feed water is 60℃and the permeate water is 10℃,the permeation flux of the direct contact membrane distillation(DCMD)process is about 35kg/(m^(2)·h),and the salt rejection rate is 99.9%.In the 200-min continuous DCMD experiment,the salt rejection rate of Janus hollow fiber membranes always remained above 98%.

关 键 词：Janus中空纤维膜 直接接触式膜蒸馏 相转化调控 表面偏析 