Intensive-visible-light-responsive ANbO_(2)N(A = Sr, Ba) synthesized from layered perovskite A_(5)Nb_(4)O_(15) for enhanced photoelectrochemical water splitting  

作　　者：Sukanya Ramaraj Jeongsuk Seo 

机构地区：[1]Departmentof Chemistry.College of Natural Sciences Chonnam National University.77 Yongbong-ro,Buk-gu Gwangju 61186,Republicof Korea

出　　处：《Journal of Energy Chemistry》2022年第5期529-537,共9页能源化学（英文版）

基　　金：financially supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government(MSIT)(2020R1C1C1006373 and 2021M3I3A1084818)。

摘　　要：Nb-based, perovskite-type oxynitrides ANb(O,N)_(3)(A = Sr, Ba) have been significantly attractive semiconductor materials for photoelectrochemical(PEC) water splitting due to their absorption abilities of intensive-visible-light. However, PEC activities of these perovskites are relatively low due to reduction of Nb species during nitridation leading to the generation of anion defects and impurity phases.Herein, we propose nitridation of A-rich, layered perovskite A_(5)Nb_(4)O_(15) as starting oxides for general synthesis of photoactive ANbO_(2)N. These layered perovskite A_(5)Nb_(4)O_(15) were completely transformed to single phase perovskite-type ANbO_(2)N by nitridation. Wavelength onsets of light absorption were observed at 700 nm for SrNbO_(2)N and at 740 nm for BaNbO_(2)N. According to X-ray photoelectron spectroscopy results,excess Lewis base A species significantly suppressed the generation of reduced species such as Nb^(4+) and Nb^(3+)during nitridation, although it led to an amorphous surface of the as-prepared oxynitride.Subsequent annealing in Ar largely enhanced surface crystallinity of ANbO_(2)N. As a result, Co(OH)_(x)/ANbO_(2)N/FTO photoanodes, prepared by loading Co(OH)_(x) electrocatalyst, showed high photocurrent density of 1.6(A = Sr) and 2.4 m A cm^(-2)(A = Ba) at 1.23 VRHEunder AM 1.5 G simulated sunlight. These results demonstrate that A-rich layered perovskite A_(5)Nb_(4)O_(15)are effective starting precursors for preparing lowdefective ANbO_(2)N, thus improving PEC water splitting activity.

关 键 词：Perovskite-type oxynitride CaNbO_(2)N SrNbO_(2)N BaNbO_(2)N A-rich starting oxide Surface heat treatment Ar annealing Solar water oxidation 