高钢级石油套管用钢连续冷却转变行为的研究  

The Research on Continuous Cooling Transformation Behavior of High Grade ERW Petroleum Casing Steel

作　　者：李睿鑫 孔进丽 王青峰[2] Li Ruixin;Kong Jinli;Wang Qingfeng(Nanjing Iron andSteel Co.,Ltd.;College of Material Science and Engineering,Yanshan University)

机构地区：[1]南京钢铁股份有限公司 [2]燕山大学材料科学与工程学院

出　　处：《宽厚板》2022年第3期1-4,共4页Wide and Heavy Plate

摘　　要：采用Gleeble热模拟技术并结合金相硬度法,对P110、Q125级别ERW石油套管试制钢的连续冷却转变行为进行研究。连续冷却转变行为表明,P110级11#试制钢只有在冷却速度≥30℃/s的条件下才能淬透获得完全马氏体组织,Q125级12#试制钢在冷却速度≥50℃/s、Q125级13#试制钢在冷却速度≥10℃/s的条件下淬透才能获得完全马氏体组织。By means of Gleeble thermal simulation technology in combination with metallographic hardness testing method,the continuous cooling transformation behavior of P110,Q125 grade ERW petroleum casing test steel is studied.The continuous cooling transformation behavior shows that the P110 grade 11#test steel can only be through-hardened to attain martensite under the condition of cooling rate≥30℃/s,while the steel can only be through-hardened to attain complete martensite structure at the cooling rate≥50℃/s for Q125 grade 12# test steel and at the cooling rate≥10℃/s for Q125 grade 13# test steel.

关 键 词：ERW 物理模拟 连续冷却转变 淬透性 

分 类 号：TG142[一般工业技术—材料科学与工程] TE931.2[金属学及工艺—金属材料]