Microstructures and coercivity mechanism of 2:17-type Sm-Co magnets with high remanence  

作　　者：Wei Sun Ming-Gang Zhu Yi-Kun Fang Zhi-Ying Liu Zhao-Hui Guo Wei Li 

机构地区：[1]Division of Functional Materials,Central Iron and Steel Research Institute,Beijing 100081,China

出　　处：《Rare Metals》2022年第4期1353-1356,共4页稀有金属（英文版）

基　　金：the National Basic Research Program of China(No.2014CB643701);the National Natural Science Foundation of China(No.51171048)。

摘　　要：Sm(Co_(bal)Fe_(0.245)Cu_(0.07)Zr_(0.02))7.8(at%)sintered magnets with high remanence(B_(r)~1.15 T)were prepared using a traditional powder metallurgy method.Tunable magnetic properties,especially intrinsic coercivity(H_(cj)),were obtained through adjusting isothermal procedure parameters.H_(cj)of the magnets increases from 305 to 752 kA·m^(-1)with isothermal annealing time increasing from 3 to 20 h,while B_(r) of the magnets almost keeps constant.From the bright field transmission electron microscopy(TEM)images,it is found that:(1)there is dispersed precipitated phase with very small size in the magnet annealed for 3 h,while the magnets annealed for 20 h have distinct and intact cellular structure;(2)the number density of Z-phase in magnet annealed for 20 h is bigger than that for 3 h.Besides,the finer microstructures were studied with high-resolution transmission electron microscopy(HRTEM).

关 键 词：MICROSTRUCTURES Coercivity mechanism 2:17-type SmCo permanent magnet 

分 类 号：TM273[一般工业技术—材料科学与工程]