新型催化裂化抗钒催化剂在MIP装置上的工业应用  

COMMERCIAL APPLICATION OF NEW V-TRAP CATALYTIC CRACKING CATALYST IN MIP UNITS

作　　者：许明德[1] 周建文[2] 张杰潇 于善青[1] 李建鹏[2] Xu Mingde;Zhou Jianwen;Zhang Jiexiao;Yu Shanqing;Li Jianpeng(SINOPEC Research Institute of Petroleum Processing,Beijing 100083;SINOPEC Jinling Company)

机构地区：[1]中国石化石油化工科学研究院,北京100083 [2]中国石化金陵分公司

出　　处：《石油炼制与化工》2022年第8期41-47,共7页Petroleum Processing and Petrochemicals

摘　　要：采用新开发的催化剂表面涂覆制备技术,制备了可用于富氧再生条件催化裂化装置的抗钒催化剂,并在中国石化金陵分公司3号催化裂化装置上进行了工业应用。应用结果表明:该催化剂具有良好的抗钒能力,在平衡剂的钒质量分数超过6000μg/g时表现出优异的催化性能;在降低剂耗的情况下,平衡剂微反活性仍提高了3以上,而且表现出优良的活性稳定性;在该催化剂作用下,催化裂化的液化气+汽油收率增加3.54百分点,柴油收率减少1.67百分点,丙烯产率(对新鲜原料)增加0.69百分点,干气中氢气/甲烷体积比降低0.23。New vanadium-trap(V-trap)catalytic cracking(FCC)catalysts that could be used in complete regenerated units were developed by using means of catalyst particles surface coating technology.The results show that the catalyst has better ability of metal tolerance and high bottoms conversion.The catalyst has been applied commercially in the third FCC unit of SINOPEC Jinling Company.The results of routine statistic data showed that the catalyst had good ability of vanadium resistance and excellent catalytic performance when the mass fraction of vanadium in the equilibrium catalyst exceeds 6000μg/g.Under the condition of reducing the catalyst consumption,the activity of the balancing agent was still increased more than 3,and showed excellent activity stability.The yield of LPG and gasoline was increased by 3.54 percentage points,the yield of LCO was decreased by 1.67 percentage points,the yield of propylene was increased by 0.69 percentage point,and the volume ratio of H_(2) and CH_(4) was obviously decreased by 0.23 percentage point.

关 键 词：催化裂化 催化剂 抗钒 

分 类 号：TE624.9[石油与天然气工程—油气加工工程]