功能树脂在带束层骨架材料粘合胶中的应用  

Application of Functional Resin in Adhesive Compound of Belt Skeleton Material

作　　者：赵之朋 徐霄平 俞正洲 郭虎 刘玉帅 ZHAO Zhipeng;XU Xiaoping;YU Zhengzhou;GUO Hu;LIU Yushuai(Shandong Yanggu Huatai Chemical Co.,Ltd,Yanggu 252300,China;National Rubber Additive Engineering Technology Research Center,Yanggu 252300,China)

机构地区：[1]山东阳谷华泰化工股份有限公司,山东阳谷252300 [2]国家橡胶助剂工程技术研究中心,山东阳谷252300

出　　处：《轮胎工业》2022年第8期486-489,共4页Tire Industry

摘　　要：研究功能树脂在带束层骨架材料粘合胶中的应用。结果表明:加入功能树脂胶料的门尼焦烧时间缩短,交联密度减小,硫化速度减慢,抗硫化返原性能提高;当间苯二酚用量减小时,加入适量功能树脂可以提高硫化胶的拉伸性能和撕裂强度,胶料的钢丝抽出力保持在正常生产配方胶料水平;当间苯二酚和功能树脂用量分别为0.5和1份时,胶料的综合性能最佳。The application of functional resin in the adhesive compound of belt skeleton material was studied.The results showed that the Mooney scorch time of the compound by adding functional resin was shortened,the crosslinking density was decreased,the vulcanization speed was slowed down,and the antireversion property was improved.When the dosage of resorcinol was decreased,adding an appropriate amount of functional resin could improve the tensile properties and tear strength of the vulcanizate,and the steel wire extraction force of the compound remained at the level of the normal production formula compound.When the dosage of resorcinol and functional resin were 0.5 and 1 phr,respectively,the comprehensive properties of the compound were the best.

关 键 词：功能树脂 间苯二酚 粘合胶 硫化特性 物理性能 粘合性能 

分 类 号：TQ330.387[化学工程—橡胶工业] TQ330.9