Effect of Co^(2+)substitution in B-sites of the perovskite system on the phase formation,microstructure,electrical and magnetic properties of Bi0.5(Na0.68K0.22Li0.10)0.5TiO3 ceramics  

作　　者：Pamornnarumol Bhupaijit Chonnarong Kaewsai Tawat Suriwong Supree Pinitsoontorn Surirat Yotthuan Naratip Vittayakorn Theerachai Bongkarn 

机构地区：[1]Department of Physics,Faculty of Science,Naresuan University,Phitsanulok 65000,Thailand [2]School of Renewable Energy and Smart Grid Technology,Naresuan University,Phitsanulok 65000,Thailand [3]Research Center for Academic Excellence in Applied Physics,Faculty of Science,Naresuan University,Phitsanulok 65000,Thailand [4]Institute of Nanomaterials Research and Innovation for Energy(IN-RIE),Khon Kaen University,Khon Kaen 40002,Thailand [5]Department of Chemistry,School of Science,King Mongkut's Institute of Technology Ladkrabang,Bangkok 10520,Thailand

出　　处：《International Journal of Minerals,Metallurgy and Materials》2022年第9期1798-1808,共11页矿物冶金与材料学报（英文版）

基　　金：financially supported by the National Science,Research and Innovation Fund(NSRF)through Naresuan University(R2564B001)。

摘　　要：Bi_(0.5)(Na_(0.68)K_(0.22)Li_(0.10))_(0.5)Ti_(1-x)Co_(x)O_(3) lead-free perovskite ceramics(BNKLT-xCo,x=0,0.005,0.010,0.015 and 0.020)were fabricated via the solid-state combustion technique.A small-amount of Co^(2+)ion substitution into Ti-sites led to modification of the phase formation,microstructure,electrical and magnetic properties of BNKLT ceramics.Coexisting rhombohedral and tetragonal phases were observed in all samples using the X-ray diffraction(XRD)technique.The Rietveld refinement revealed that the rhombohedral phase increased from 39%to 88%when x increased from 0 to 0.020.The average grain size increased when x increased.With increasing x,more oxygen vacancies were generated,leading to asymmetry in the bipolar strain(S-E)hysteresis loops.For the composition of x=0.010,a high dielectric constant(ε_(m))of 5384 and a large strain(S_(max))of 0.23%with the normalized strain (d*_(33))of 460 pm·V^(-1) were achieved.The BNKLT-0Co ceramic showed diamagnetic behavior but all of the BNKLT-xCo ceramics exhibited paramagnetic behavior,measured at 50 K.

关 键 词：BNKLT-xCo dielectric FERROELECTRIC strain magnetic 

分 类 号：TQ174.1[化学工程—陶瓷工业]