1960 MPa锌-铝合金镀层钢丝及主缆索股抗疲劳性能试验研究  被引量:1

Experimental study on fatigue resistance of 1960 MPa zinc-aluminum alloy coated steel wire and main cable strand

在线阅读下载全文

作  者:蔡科瀚尔 薛花娟 Cai Kehaner;Xue Huajuan(Hubei Communications Investment Logistics Co.,Ltd.,Wuhan 430050,China;Jiangsu Fasten Cable Co.,Ltd.,Jiangyin 214433,China)

机构地区:[1]湖北交投物流集团有限公司,湖北武汉430050 [2]江苏法尔胜缆索有限公司,江苏江阴214433

出  处:《金属制品》2022年第4期54-58,共5页Metal Products

基  金:广东省重点领域研发计划项目-重大跨海通道全寿命安全保障关键技术资助项目(项目编号:2019B111106002)。

摘  要:通过常规试验研究φ5.0 mm 1960 MPa锌-铝合金镀层钢丝以及127-φ5.0 mm锌铝合金镀层钢丝索股的抗疲劳性能,探讨桥梁缆索用高强度钢丝疲劳失效的特点和主缆疲劳寿命预估曲线,给全寿命周期内主缆钢丝及索股的疲劳寿命估算分析提供参考依据。The fatigue resistance of diameter 5.0 mm 1960 MPa zinc-aluminum alloy coated steel wire and 127 diameter 5.0 mm zinc-aluminum alloy coated steel wire strands was studied by conventional test,fatigue failure characteristics of high strength steel wire for bridge cables and fatigue life prediction curve of main cable were discussed,reference for fatigue life estimation and analysis of main cable steel wire and cable strands in whole life cycle is provided.

关 键 词:锌铝合金镀层 索股 疲劳应力幅 疲劳强度 断丝率 

分 类 号:TG356.45[金属学及工艺—金属压力加工]

 