Enhancement of Microstructure and Mechanical Property of AlSi10Mg-Er-Zr Alloys Fabricated by Selective Laser Melting

作　　者：杨天野 崔丽[1] 贺定勇[1] 黄晖[1] YANG Tianye;CUI Li;HE Dingyong;HUANG Hui(Faculty of Materials and Manufacturing,Beijing University of Technology,Beijing 100124,China)

机构地区：[1]北京工业大学材料与制造学部,北京100124

出　　处：《金属学报》2022年第9期1108-1117,共10页Acta Metallurgica Sinica

基　　金：国家自然科学基金项目No.51621003。

摘　　要：采用气雾化制粉技术原位合金化制备了AlSi10Mg-Er-Zr粉末,研究了选区激光熔化(SLM)成形AlSi10Mg-Er-Zr试样的相对密度、微观组织和力学性能。结果表明,SLM成形AlSi10Mg-Er-Zr试样的相对密度为99.20%,显微硬度为156.5 HV,室温抗拉强度达到461 MPa,屈服强度为304 MPa,相对于常规AlSi10Mg试样显微硬度提升了25.8%,抗拉强度和屈服强度分别提高了22.6%和26.7%。这是由于Er、Zr元素的加入,细化了SLM成形AlSi10Mg-Er-Zr试样的晶粒尺寸,并且使α-Al基体中Si元素的固溶度增加,由细晶强化和固溶强化机制共同作用提高了AlSi10Mg-Er-Zr合金的力学性能。The AlSi10Mg alloy fabricated using selective laser melting(SLM)has attracted attention because of its excellent quality and properties.However,the mechanical properties of SLM AlSi10Mg alloy cannot meet the requirements of the high strength of aluminum alloys in the aerospace industry.To improve the mechanical properties of SLM AlSi10Mg alloy,AlSi10Mg-Er-Zr powders were prepared using in situ alloying mechanism and gas atomization.The relative density,microstructure,and mechanical properties of SLM AlSi10Mg-Er-Zr alloys have been investigated.The results show that the relative density of AlSi10Mg-Er-Zr alloys fabricated using SLM reaches 99.20%.The SLM AlSi10Mg-Er-Zr alloy has a microhardness value of 156.5 HV.The ultimate tensile strength(UTS)and yield strength(YS)of the SLM AlSi10Mg-Er-Zr alloy can reach 461 and 304 MPa,respectively.Compared with the conventional AlSi10Mg alloy,the microhardness has been increased by 25.8%;the UTS and YS are increased by 22.6%and 26.7%,respectively.The fine-grain and solid solution strengthening associated with SLM processing with the addition of Er and Zr elements,as a result of increased grain size refinement and solid solubility of Si element in theα-Al matrix,are responsible for the improvement in the mechanical properties.

关 键 词：选区激光熔化 AlSi10Mg-Er-Zr合金 稀土元素 显微组织 力学性能 