基于试样重组技术的RPV钢断裂性能研究  

Study on fracture properties of RPV material based on specimen reconstitution technology

作　　者：黄平[1] 祁爽 吕云鹤 范敏郁 贾文清 钱王洁 蔡可信 张晏玮[1] 彭群家 HUANG Ping;QI Shuang;LÜYunhe;FAN Minyu;JIA Wenqing;QIAN Wangjie;CAI Kexin;ZHANG Yanwei;PENG Qunjia(Suzhou Nuclear Power Research Institute,Suzhou 215004,China;Nuclear and Radiation Safety Center,Beijing 100082,China)

机构地区：[1]苏州热工研究院有限公司,江苏苏州215004 [2]生态环境部核与辐射安全中心,北京100082

出　　处：《中国测试》2022年第9期158-163,共6页China Measurement & Test

基　　金：国家重点研发计划资助(2020YFB1901500);国家自然科学基金(U1867215);江苏省政策引导类计划(BZ2020057)。

摘　　要：反应堆压力容器(reactor pressure vessel,RPV)的辐照脆化程度主要通过定期取出的辐照监督试样的试验结果进行评价,由于受辐照监督管空间的限制,监督样品的尺寸和数量非常有限,试样重组技术可高效率利用有限的辐照监督材料获取可靠的材料断裂韧性数据。该文针对反应堆压力容器原始态材料16MND5,开展基础力学性能测试,包含拉伸、冲击及断裂韧性,确定材料基本力学性能。在开展RPV材料断裂韧性试验时利用数字图像相关(digital image correlation,DIC)技术获取试验过程中试样表面应变演化规律和塑性区范围,基于ANASYS有限元分析软件计算加载过程中最大塑性区范围,有限元分析结果与试验结果较为吻合,为后续试样重组确定其可再次利用的材料范围。The irradiation embrittlement degree of reactor pressure vessel(RPV) was mainly evaluated by the test results of irradiation surveillance specimens taken out regularly. Due to the limitation of irradiation surveillance capsules space, the size and quantity of surveillance specimens were limited. In consequence, the limited irradiation surveillance materials could be used efficiently by the specimen reconstitution technology to obtain reliable material fracture toughness data. In this paper, original RPV materials 16MND5 were subjected on tensile, impact and fracture toughness tests to investigate the basic mechanical properties. Meanwhile, the digital image correlation(DIC) technology was applied in fracture toughness tests to obtain the surface strain evolution law and plastic zone range of the compact tension specimen. In addition, for comparison with DIC results, the surface strain evolution law was also calculated based on the finite element analysis to the maximum plastic zone size during the loading process. The results indicated that the finite element analysis results were in good agreement with the test results, so as to determine the reusable material range for the specimen reconstitution technology. More important, the plastic zone range was limited and thus there were enough range for specimen reconstitution. The fracture toughness of reconstituted specimens should be equal to that of the specimens of original RPV materials, so the reconstituted specimens can be used to obtain the fracture toughness of the RPV materials, thus solving the practical engineering problem of insufficient surveillance specimens.

关 键 词：辐照监督试样 反应堆压力容器 试样重组技术 断裂韧性 数字图像相关技术 塑性区 