无水硫酸钙晶须的制备及表征  

Preparation and characterization of anhydrous calcium sulfate whisker

作　　者：齐源昊 吴锦绣[1,2,3] 柳召刚 胡艳宏[1,2,3] 冯福山 李健飞[1,2,3] 王昕 刘丛林 QI Yuanhao;WU Jinxiu;LIU Zhaogang;HU Yanhong;FENG Fushan;LI Jianfei;WANG Xin;LIU Conglin(School of Materials and Metallurgy,Inner Mongolia University of Science and Technology,Baotou 014010,China;Green Extraction and Efficient Utilization of Light Rare Earth Resources Key Laboratory of Ministry of Education;Inner Mongolia Autonomous Region Rare Earth Hydrometallurgy and Light Rare Earth Application Key Laboratory)

机构地区：[1]内蒙古科技大学材料与冶金学院,内蒙古包头014010 [2]轻稀土资源绿色提取与高效利用教育部重点实验室 [3]内蒙古自治区稀土湿法冶金与轻稀土应用重点实验室

出　　处：《无机盐工业》2022年第10期109-115,共7页Inorganic Chemicals Industry

基　　金：国家自然科学基金(51965053,51634005);内蒙古自然科学基金(2021LHMS05018,2022LHMS05022)。

摘　　要：以某稀土厂生产过程中产生的硫酸铵废水为原料,用氯化钙作为钙源,采用水热法制备高长径比的硫酸钙晶须。首先采用正交实验研究反应时间、反应温度和陈化时间对硫酸钙晶须长径比的影响,确定最佳工艺条件。在正交实验最佳工艺条件的基础上,研究了pH对制备硫酸钙晶须形貌的影响。使用扫描电子显微镜(SEM)、X射线衍射仪(XRD),红外分析仪(FT-IR)和热重-差热分析仪(TG-DSC)对制得的硫酸钙晶须的表面形貌和物相进行了表征和分析。研究结果表明:在制备硫酸钙晶须的最佳工艺条件下(即反应时间为5 h、反应温度为140℃、陈化时间为4.5 h),溶液体系pH为1时,制备得到纯态无水硫酸钙晶须,其形貌最佳、长径比最大,平均长度达到117.44μm、平均长径比为40.2。Calcium sulfate whiskers with high aspect ratio were prepared by hydrothermal method using ammonium sulfate wastewater produced in the production process of a rare earth plant as raw material and calcium chloride as calcium source.Firstly,the effects of reaction time,reaction temperature and aging time on the aspect ratio of calcium sulfate whisker were studied by orthogonal experiment to determine the optimal process conditions.Based on the optimal process conditions of or‐thogonal experiment,the effect of pH value on the morphology of calcium sulfate whiskers was studied.The surface morphol‐ogy and phase of calcium sulfate whiskers were characterized and analyzed by scanning electron microscopy(SEM),X-ray diffraction(XRD),infrared analyzer(FT-IR)and thermogravimetric‐differential thermal analyzer(TG-DSC).The results showed that the optimum preparation conditions of calcium sulfate whisker were reaction time of 5 h,reaction temperature of 140°C,aging time of 4.5 h.When the pH value of the solution system was 1,pure anhydrous calcium sulfate whiskers were prepared,which had the best morphology and high aspect ratio.The average length was 117.44μm and the average as‐pect ratio was 40.2.

关 键 词：硫酸铵废水 硫酸钙晶须 水热法 长径比 