作 者:薛佳威 张博睿 吴永鹏 陈雨来 余伟[1,2] XUE Jia-wei;ZHANG Bo-rui;WU Yong-peng;CHEN Yu-lai;YU Wei(Institute of Engineering Technology,University of Science and Technology Beijing,Beijing 100083,China;National Engineering Technology Research Center of Advanced Equipment for Strip Production,University of Science and Technology Beijing,Beijing 100083,China;Ningbo Iron and Steel Company Technology Center,Zhejiang Ningbo 315800,China)
机构地区:[1]北京科技大学工程技术研究院,北京100083 [2]北京科技大学国家板带生产先进装备工程技术研究中心,北京100083 [3]宁波钢铁公司技术中心,浙江宁波315800
出 处:《表面技术》2022年第10期269-275,335,共8页Surface Technology
摘 要:目的为了明确层流冷却浊环水中Cl^(-)质量浓度对SPHC钢板腐蚀的影响,提高SPHC钢板在潮湿环境下存放发生腐蚀后的表面质量。方法通过全浸腐蚀试验进行模拟。已有研究表明层流冷却浊环水中Cl^(-)的质量浓度与钢板表面Cl^(-)的残留量呈线性正比关系,因此设置不同Cl^(-)质量浓度对SPHC钢板的腐蚀行为进行研究。通过数码相机、扫描电镜和激光共聚焦显微镜分析宏观腐蚀形貌和腐蚀坑形貌,采用失重法测量不同Cl^(-)质量浓度下的均匀腐蚀速率,电化学测试分析不同Cl^(-)质量浓度下覆盖腐蚀产物膜试样的电化学特征。结果Cl^(-)质量浓度为60、300、1000 mg/L时,均匀腐蚀速率都呈现先增大后减小的趋势,这是点蚀的形成扩展和腐蚀产物的缓蚀作用所致。Cl^(-)质量浓度升高,穿过基体表面的离子增多,缩短了点蚀形成和扩展的时间,均匀腐蚀速率增大。Cl^(-)质量浓度的升高使得基体表面钝化膜被加速破坏,腐蚀电流密度增大,形成的锈层极易被溶解,阻抗值上下波动,这种情况下形成的锈层对基体不具有保护作用。结论降低层流冷却浊环水中Cl^(-)的质量浓度是提高潮湿环境下腐蚀后SPHC钢板表面质量的有效途径。The surface quality of steel products has always been a major concern.In the steel rolling process,in order to reduce production costs,laminar flow cooling of steel plates is often performed using recyclable water treated by turbid ring water systems.Due to the rapid evaporation of water during the cooling process,there will be some ions left on the surface of the steel plate,which will make the steel plate corrosive in the later storage process.In order to clarify the effect of the concentration of Cl^(-)in laminar cooling turbid ring water on the corrosion of SPHC steel plates,so as to improve the surface quality of SPHC steel plates after corrosion occurs when they are stored in a humid environment,simulations were performed by full immersion corrosion tests.It was shown that the concentration of Cl^(-)in the laminar cooling turbid ring water showed a linear and positive relationship with the residual amount of Cl^(-)on the surface of steel plates,so the corrosion behavior of SPHC steel plates was studied by setting different concentrations of Cl^(-).The macroscopic corrosion morphology of the specimens was analyzed by digital camera.The surface morphology and depth of corrosion pits on the specimens were analyzed by scanning electron microscopy and laser confocal microscopy,respectively.The loss-in-weight method was used to measure the uniform corrosion rate for different concentrations of Cl^(-).Electrochemical tests were performed to analyze the electrochemical characteristics of specimens covered with corrosion product films at different concentrations of Cl^(-).The results show that whether the concentration of Cl^(-)is 60 mg/L,300 mg/L or 1000 mg/L,the uniform corrosion rate shows a trend of increasing first and then decreasing,which is caused by the formation and expansion of pitting corrosion in the early and middle stages of corrosion and the corrosion retardation of corrosion products in the late stages of corrosion.The increase in the concentration of Cl^(-)increases the number of ions crossing the
关 键 词:SPHC钢板 全浸腐蚀试验 Cl‒质量浓度 腐蚀行为 电化学 表面质量
分 类 号:TG172[金属学及工艺—金属表面处理]