阻燃有机玻璃FRPMMA的制备工艺研究  

Preparation of flame retardant polymethyl methacrylate

作　　者：胡晓蕾 张淼 王双庆 鲁俊[1] HU Xiao-lei;ZHANG Miao;WANG Shuang-qing;LU Jun(Hubei Key Laboratory of Power System Design and Test for Electrical Vehicle,Xiangyang 441053,China)

机构地区：[1]纯电动汽车动力系统设计与测试湖北省重点实验室湖北文理学院,湖北襄阳441053

出　　处：《应用化工》2018年第S02期91-92,95,共3页Applied Chemical Industry

基　　金：湖北省自然科学基金项目(2015CFC806);纯电动汽车动力系统设计与测试湖北省重点实验室基金(HBUASEV2015F013)。

摘　　要：阻燃有机玻璃FRPMMA制备工艺中,存在无机阻燃剂粒子在基体中相容性差问题。通过偶联剂进行氢氧化镁粒子表面改性和超声处理添加工艺,将处理后的无机阻燃剂加入甲基丙烯酸甲酯溶液,以过氧化苯甲酰为引发剂,70℃下进行分段本体聚合,制备低成本阻燃FRPMMA。扫描电镜SEM图片显示氢氧化镁分散效果良好,燃烧实验结果FRPMMA限氧指数达29。Aiming at low compatibility of inorganic flame retardant in monomer substrate during the preparation of flame retardant polymethyl methacrylate,the process was designed by modifying Mg(OH)2 with coupling reagent and novel supersonic feeding,polymerizing at 70℃initiated by benzoyl peroxide.The results of SEM showed good dispersity of Mg(OH)2 and the limited oxygen index was 29.

关 键 词：阻燃FRPMMA 表面改性 超声 相容性 