Synthesis,structural investigation,dielectric and magnetic properties of Zn^(2+)-doped cobalt ferrite by the sol-gel technique  

作　　者：Mohammad Sajjad Hossain MdBadiul Alam Mohammad Shahjahan Most.Hosney Ara Begum MdMoazzem Hossain Suravi Islam Nazia Khatun Mukul Hossain Mohammad Saiful Alam Md.Al-Mamun 

机构地区：[1]Industrial Physics Division,BCSIR Laboratories Dhaka BCSIR,Dhaka 1205,Bangladesh [2]Noakhali Science and Technology University Noakhali 3814,Bangladesh [3]Daffodil International University Dhaka 1205,Bangladesh [4]Atomic Energy Centre Dhaka Dhaka 1000,Bangladesh

出　　处：《Journal of Advanced Dielectrics》2018年第4期54-59,共6页先进电介质学报（英文）

摘　　要：Zinc substituted cobalt ferrite nanoparticles with elemental composition Co_(1-x)Zn_(x)Fe_(2)O_(4)(x=0.0,0.2,0.4,0.6)were prepared by the sol-gel auto-combustion technique using Co,Fe,Zn nitrate as a precursor where nitrates to citrate was 1:3.The as prepared powder of cobalt zinc ferrite was sintered at 900○C for 3 h.Structural,morphological,dielectric and magnetic properties were studied by x-ray diffractometer(XRD),scanning electron microscope(SEM),high precision impedance analyzer and vibrating sample magnetometer(VSM),respectively.The peaks obtained from the XRD confirmed samples having crystallite(32–36 nm)single phase inverse spinel structure without any traceable impurity.Lattice parameters were calculated from XRD and it increases with Zn content.SEM revealed irregularly shaped grains(-0.5–0.7μm)morphology with heterogeneous distribution.The dielectric constant(ε′)and dielectric loss(tanδ),have been measured as a function of frequency at room temperature.The dependence of ε′ and tan δ with frequency showed the normal dielectric behavior in accordance with the Maxwell-Wagner type of interfacial polarization and electron hopping change between Co^(2+)and Co^(3+)as well as between Fe^(2+)and Fe^(3+)ions at octahedral sites.

关 键 词：SOLGEL cobalt ferrite DIELECTRIC magnetic properties. 

分 类 号：TG1[金属学及工艺—金属学]