活性元对低附带毁伤弹药的近场超压增强效应  

Effect of Near-Field Overpressure Enhancement of Reactive Material on Low Collateral Damage Ammunition

作　　者：杨秉妍 范瑞军 江自生 皮爱国[1] 王金英 YANG Bingyan;FAN Ruijun;JIANG Zisheng;PI Aiguo;WANG Jinying(State Key Laboratory of Explosion Science and Technology,Beijing Institute of Technology,Beijing 100081,China;Jiangnan Industry Group Co.,Ltd.,Xiangtan 411207,Hunan,China;School of Environment and Safety Engineering,North University of China,Taiyuan 030051,Shanxi,China)

机构地区：[1]北京理工大学爆炸科学与技术国家重点实验室,北京100081 [2]江南工业集团有限公司,湖南湘潭411207 [3]中北大学环境与安全工程学院,山西太原030051

出　　处：《高压物理学报》2022年第6期162-170,共9页Chinese Journal of High Pressure Physics

摘　　要：为了实现低附带毁伤弹药的近场爆炸威力增强效应,提出在分装式低附带毁伤弹药的重金属颗粒嵌层中加入活性元成分,以期增强近场超压与比冲量。开展了不同含量活性元的静爆实验,利用自由场压力测试系统测得爆炸后近场及中远场的冲击波压力曲线。结果表明:在重金属颗粒嵌层中加入一定含量的活性元后,冲击波超压峰值和比冲量在37.5倍装药直径处分别提高31.6%和21.3%。根据实验结果,利用数值模拟确定了Miller反应速率模型参数,讨论了活性元后燃反应能量释放规律以及活性元组分反应度随时间的变化关系,在充分燃烧的理想情况下,活性元二次燃烧持续时间可达300 ms,且活性元含量区间极有可能存在最优配比。研究结果可为分装式低附带毁伤武器的近场冲击波区域增强效应及其工程化设计提供参考。To realize the effect of the near-field shock wave enhancement of low collateral damage ammunition,this study proposes to add reactive material into the embedding layer of heavy metal particle in the sub-package low collateral damage ammunition to enhance the near-field overpressure and specific impulse.Static explosion experiments with different contents of reactive material were carried out,and the pressure curves of the near field and the mid-far field shock wave after the explosion were measured by the free field pressure test system.The results show that:after adding a certain content of reactive material into the heavy metal particle intercalation,the peak value of the overpressure and the specific impulse of shock wave at 37.5 times charge diameter are increased by 31.6%and 21.3%,respectively.According to the experimental results,the parameters of the Miller reaction rate model were determined by numerical simulation,and the law of energy release after-combustion reaction of the active element and the timedependent change of the reactivity of the reactive material components were discussed.The duration of the secondary combustion can reach 300 ms under the ideal situation of sufficient combustion,and an optimal proportion of the range of reactive material content is likely exist.This research provides considerable development direction and application prospects for the regional enhancement effect of near-field shock wave and its engineering design of sub-packaged low collateral damage weapons.

关 键 词：活性元 重金属颗粒嵌层 冲击波超压 毁伤效应 

分 类 号：O389[理学—流体力学] TJ55[理学—力学]