酸浸活化硼泥提镁的研究  

Extraction of Magnesium from Activated Boron Mud by Acid Leaching

作　　者：王立杰 宁志强 谢宏伟 宋秋实 尹华意 Wang Lijie;Ning Zhiqiang;Xie Hongwei;Song Qiushi;Yin Huayi(Institute of metallurgy,Northeastern University,Shenyang 110819,China)

机构地区：[1]东北大学冶金学院,辽宁沈阳110819

出　　处：《稀有金属》2022年第9期1207-1214,共8页Chinese Journal of Rare Metals

基　　金：国家自然科学基金项目(51204037);中央高校基本科研业务费(N140204016)资助。

摘　　要：硼泥是硼化工行业产生的固体废弃物,以酸浸法提取硼泥中的镁元素,对硼泥进行预处理以促进其中氧化镁的浸出。分别以活化和未活化硼泥为原料,研究了酸浸温度(T)、酸浸时间(t)、硫酸浓度(ω)和液固比(L/S)对酸浸硼泥实验中氧化镁浸出率的影响,用正交试验确定了影响硼泥中氧化镁浸出率的主次因素,利用化学分析、X射线衍射(XRD)和扫描电镜(SEM)对两种原料、结晶产物和浸出渣分别进行化学成分、物相组成和微观形貌的表征分析。结果表明,对硼泥进行活化焙烧,改变了硼泥的形貌和物相组成,提高了氧化镁的浸出率;直接冷却析出的晶体为符合国家标准的饲料级七水硫酸镁;酸浸渣的主要成分为无定型二氧化硅,可用于制备白炭黑。实验确定了以活化硼泥为原料时优化的酸浸工艺条件:酸浸温度为95℃,酸浸时间为2.0 h,硫酸浓度为50%,L/S为3∶1 ml·g^(-1),搅拌速度为400 r·min^(-1),在此酸浸条件下活化硼泥中氧化镁的浸出率为94.63%,与未活化硼泥相比,活化处理有利于硼泥中氧化镁的浸出,可以减少酸浸过程中硫酸的用量,氧化镁浸出量提高了20.80%;当两者浸出率相似时,硫酸用量减少约20%。Boron mud was solid waste produced by boron chemical industry.Due to the low grade sedimentary metamorphic boron deposits in Northeast China.A large amount of alkaline slag was produced in the production of borax,which directly polluted the environment.About 40%of magnesium oxide was contained in boron mud.Acid leaching method was used to recover magnesium from boron mud.However,the boron mud was directly acid-leached to extract magnesium oxide,and a large amount of sulfuric acid was consumed in the acid-leaching process.Because there was a large amount of MgCO_(3) in the boron mud,the reaction was violent at the beginning of the experiment,and a large amount of CO_(2) was generated,which made the leachate easy to overflowed.Therefore,the boron mud was pretreated to promote the leaching of MgO and reduce the amount of sulfuric acid in the experiment.Explore the effect of activation pretreatment of boron mud on the leaching of MgO from it.Boron mud contains MgCO_(3)and Mg_(2)SiO_(4).After high temperature activation,MgCO_(3) released CO_(2) and turned into MgO,which could not only improve the reactivity,but also reduce the risk of the leachate overflow in the test.Different concentrations of sulfuric acid solution were prepared according to the set conditions,and the boron mud was activated at the set activation temperature.Grinding and magnetic separation of the two kinds of boron mud to reduce the influence of impurity element iron on the purity of crystals.Activated and unactivated boron mud were selected as raw materials.The effects of acid leaching temperature(T),acid leaching time(t),sulfuric acid concentration(ω)and liquid-solid ratio(L/S)on the leaching rate of MgO from boron mud were studied.Under the same experimental conditions,the change of magnesium oxide leaching rate between activated boron mud and unactivated boron mud was studied in this experiment.The primary and secondary factors affecting the leaching rate of magnesium oxide from boron mud were determined by orthogonal test.The concentration o

关 键 词：硼泥 活化 酸浸 

分 类 号：TQ110.9[化学工程—无机化工]