Development of a new high-shear and low-pressure grinding wheel and its grinding characteristics for Inconel718 alloy  

作　　者：Bing LIU Yebing TIAN Jinguo HAN Linguang LI Zhiqiang GU Xintao HU 

机构地区：[1]School of Mechanical Engineering,Shandong University of Technology,Zibo 255049,China [2]Institute for Advanced Manufacturing,Shandong University of Technology,Zibo 255049,China

出　　处：《Chinese Journal of Aeronautics》2022年第12期278-286,共9页中国航空学报（英文版）

基　　金：supported by the National Natural Science Foundation of China(Nos.51875329 and 51905322);China postdoctoral Science Foundation(No.2021T140420);Taishan Scholar Special Foundation of Shandong Province(No.tsqn201812064);Shandong Provincial Natural Science Foundation(No.ZR2017MEE050);Shandong Provincial Key Research and Development Project(No.2018GGX103008);Scientific Innovation Project for Young Scientists in Shandong Provincial Universities(No.2019KJB030);Key Research and Development Project of Zibo City(No.2019ZBXC070).

摘　　要：Nickel-based alloy has been widely used due to its outstanding mechanical properties.However, Nickel-based alloy is a typical difficult-to-machine material, which is a great constrain for its application in the manufacturing field. To improve the surface quality of the ground workpiece, a new high-shear and low-pressure grinding wheel, with high ratio of tangential grinding force to normal grinding force, was fabricated for the grinding of selective laser melting(SLM) manufactured Inconel718 alloy. The principle of high-shear and low-pressure grinding process was introduced in detail, which was quite different from the conventional grinding process. The fabrication process of the new grinding wheel was illustrated. A serial of experiments with different processing parameters were carried out to investigate the grinding performance of the developed grinding wheel via analyzing surface roughness and surface morphology of the ground workpiece.The optimal processing parameters of high-shear and low-pressure grinding were obtained. The surface roughness of ground workpiece was reduced to 0.232 μm from the initial value of 0.490 μm under the optimal grinding conditions. It was found that the initial scratches on the ground workpiece were almost completely removed after the observations with the metalloscopy and the fieldemission scanning electron microscopy(FE-SEM). The capability of the newly developed highshear and low-pressure grinding wheel was validated.

关 键 词：GRINDING Grinding wheel High-shear and low-pressure grinding Inconel718 alloy Selective laser melting(SLM) 

分 类 号：V261[航空宇航科学与技术—航空宇航制造工程] TG743[金属学及工艺—刀具与模具] TG580.6