ER70S-6焊丝钢盘条拉拔断裂原因分析与改善  被引量:3

Analysis and improvement of drawing fracture of ER70S-6 welding wire steel

在线阅读下载全文

作  者:曹磊[1] 郭峰[2] 纪文杰[1] CAO Lei;GUO Feng;JI Wenjie(Steel Rolling Mill,Jiangsu YongGang Group Co.,Ltd.,Zhangjiagang 215628,China;R&D Department,Jiangsu YongGang Group Co.,Ltd.,Zhangjiagang 215628,China)

机构地区:[1]江苏永钢集团有限公司轧钢厂,江苏张家港215628 [2]江苏永钢集团有限公司产品研发中心,江苏张家港215628

出  处:《物理测试》2022年第6期46-50,共5页Physics Examination and Testing

摘  要:ER70S-6焊丝钢盘条在精拉过程中出现断裂,对盘条进行了微观组织观察。结果表明:盘条拉拔断裂是由于拉拔过程中异常组织不能与珠光体+铁素体组织协同变形导致裂纹产生,继而扩展断裂。通过控制连铸过程中的成分偏析以及优化轧制过程中的控轧控冷工艺,异常组织得到了有效控制。ER70S-6 welding wire rod broke during the fine drawing process. The microstructure of the wire rod was observed. The results showed that the drawing fracture of wire rod was caused by the abnormal microstructure, which could not deform synergistically with the pearlite + ferrite microstructure in the drawing process. Therefore, the cracks propagated and the fracture was caused. By controlling the segregation of components in the continuous casting process and optimizing the controlled rolling and controlled cooling process in the rolling process, the abnormal microstructure had been effectively decreased.

关 键 词:ER70S-6 焊丝钢 拉拔断裂 成分偏析 异常组织 

分 类 号:TG422.3[金属学及工艺—焊接]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象