锌酞菁接枝纤维素纳米纤维膜的制备及其染料降解性能  

Preparation of zinc phthalocyanine grafted cellulose nanofiber and its dye degradation properties

作　　者：王占凯 徐世龙 杨世玉 胡毅[1] 胡柳 WANG Zhankai;XU Shilong;YANG Shiyu;HU Yi;HU Liu(College of Textile Science and Engineering,Zhejiang Sci-Tech University,Hangzhou 310018,China;Zhejiang Jili New Material Co.,Ltd.,Shaoxing 312000,China)

机构地区：[1]浙江理工大学纺织科学与工程学院,杭州310018 [2]浙江技立新材料股份有限公司,浙江绍兴312000

出　　处：《现代纺织技术》2023年第1期204-212,共9页Advanced Textile Technology

基　　金：绍兴市柯桥区科技攻关项目(2021JBGS304)。

摘　　要：针对现有染料光催化降解技术中存在的难回收、循环性差、需紫外光照射等问题,本文制备了一种有机光敏剂接枝纳米纤维膜材料用于染料的高效可见光催化降解。首先利用静电纺丝技术制备纳米乙酸纤维素膜,然后在碱液中水解制备再生纤维素膜(HCA),接着将合成的四羧基锌酞菁光敏剂(CZnPc)通过酯化反应共价接枝到HCA,得到CZnPc功能化纤维素纳米纤维膜(CZnPc-HCA)。采用红外光谱、核磁共振氢谱、质谱与扫描电子显微镜等表征结构和表观形貌,并研究了CZnPc-HCA的光敏活性。结果表明:CZnPc-HCA具有优异的单线态氧产生性能;经氙灯照射90 min,亚甲基蓝初始质量浓度为4 mg/L时,CZnPc-HCA膜(3 cm×3 cm)对其降解率达到75%以上。In recent years,wastewater discharge accounts for a large proportion of environmental pollution,posing a great threat to the environment and human health.Printing and dyeing wastewater has been paid much attention in the field of wastewater treatment and reuse for its high chroma,complex components and large amounts of discharge.The available dye-degradation methods including physical adsorption and biological treatment have problems like secondary pollution,high cost and energy-consuming,while the photocatalytic dye-degradation method based on the inorganic semiconductor,though famous for its high efficiency,also has defects such as difficult material recovery and requiring UV light illumination.Therefore,it is necessary to develop new recyclable photocatalytic materials for efficient dye decomposition in wastewater treatment.In order to construct highly-efficient,recyclable and visible light responsive dye degradation materials,we started from the excellent photocatalytic performance of organic photosensitizers and the high specific surface area of nanofiber membrane,synthesizing and characterizing tetracarboxyl modified symmetric zinc phthalocyanine organic photosensitizer,and then covalently grafted it onto the cellulose nanofiber obtained by electrospinning technology via N,N’-carbonyldiimidazole catalytic esterification method.The zinc phthalocyanine photosensitive group has strong visible light absorption and high singlet oxygen quantum yield.However,due to the high planarity of the structure,the intermolecular aggregation can lead to the reduction of photosensitive activity.In this paper,zinc phthalocyanine photosensitizer was covalently loaded on the surface of nanofiber membrane to provide space for molecular extension,which could reduce the aggregation of zinc phthalocyanine derivatives and improve the photosensitivity.The chemical structure and appearance of the novel zinc phthalocyanine functionalized nanofiber membrane were analyzed,its photocatalytic mechanism was further studied through reactive

关 键 词：光敏剂 锌酞菁 纤维素 纳米纤维膜 单线态氧 染料降解 

分 类 号：TS190.3[轻工技术与工程—纺织化学与染整工程]