有机钼添加剂对不同基底材料的摩擦学性能研究  

Tribological Properties of Molybdenum Additives on Different Substrates

作　　者：凌燕丽 李小磊 邹洋 戴媛静 LING Yanli;LI Xiaolei;ZOU Yang;DAI Yuanjing(Research Institute of Lubrication,Tianjin Research Institute for Advanced Equipment,Tsinghua University,Tianjin 300300,China;State Key Laboratory of Tribology,Tsinghua University,Beijing 100084,China;Laboratory of Ji Hua,Guangdong Foshan 528200,China)

机构地区：[1]清华大学天津高端装备研究院润滑技术研究所,天津300300 [2]清华大学摩擦学国家重点实验室,北京100084 [3]季华实验室,广东佛山528200

出　　处：《摩擦学学报》2022年第6期1161-1171,共11页Tribology

基　　金：河北省创新能力提升计划项目(19244006D);国家重点研发计划(2018YFB2002204,2020YFB2010601,2020YFB2010602,2020YFA0711000);国家自然科学基金项目(51805291);贵州省科技重大专项(黔科合重大专项字[2019]3016号);国防基础科研项目(JCKY2020110B007)资助。

摘　　要：在不同温度、载荷和速度条件下,考察非硫磷油溶性有机钼(SPFMo)添加剂对发动机低黏度润滑油(0W-20)在轴承钢、铝合金以及钛合金等五种不同材料表面摩擦学性能的影响.采用三维共聚焦激光显微镜和扫描电子显微镜(SEM)对不同基底材料磨痕的形貌、磨损体积和元素成分进行测量和分析.结果表明:在五种材料表面,SPFMo均可明显提高0W-20的减摩抗磨性能.温度越高,SPFMo的作用效果越明显,除钛合金外四种材料的摩擦系数最高可降低18%~23%;五种材料的摩擦系数和磨损率均随着载荷的升高而升高;随着摩擦速度的升高,五种材料的摩擦系数呈现出不同的变化规律,但磨损率均随摩擦速度的升高而升高.研究结果可为新型发动机的润滑油选用和设计提供有力的技术支撑和理论参考.The effects of sulfur and phosphorus free organic molybdenum(SPFMo)on the tribological properties of lubricating oil(0W-20)on five kinds of different metals(bearing steel(GCr15),aluminium alloy(7A60),titanium alloy(TC4),copper(T2),and gray iron(HT300))were investigated under different conditions including temperatures,loads and frequencies.3D measuring laser microscope and scanning electron microscopy were used to measure and analyze the morphology and wear of the five metals.The results showed that SPFMo obviously improved the anti-friction properties of 0W-20 on the five metals.Among them,the friction coefficient of 0W-20 on the bearing steel was reduced by 23%,and the wear rate was maximally dropped by 91%.With the increase of temperature,the friction coefficient of7A60 first increased and then decreased while the wear rate increased.The wear rate and friction coefficient of other materials increased with the increase of temperature.Additionally,with the increase of temperature,the effect of SPFMo on anti-friction and anti-wear was more obvious.The friction coefficient of four materials except TC4,can be reduced by 18%~23%.As for TC4,SPFMo had better anti-friction effect at lower temperature(≤40℃).When the temperature was higher than 40°C,the titanium surface wasa severely worn,and the wear rate increased by 1000 times.Small amount of S,Mo and other elements were detected on the wear tracks.This indicated that the lubrication film containing Mo,S,and O elements was generated in the friction process due to the addition of SPFMo.With the increase of load,the friction coefficient and wear rate of all materials increased.The increase of friction coefficient was most obvious on the T2 and TC4.With the addition of SPFMo,the friction coefficient of 0W20 on TC4 increased dramatically as the load exceeded 100 N.It had a sudden change and an increase of about 104 times as the load was higher than 100 N,which was related to the destruction of titanium oxide layer.With the increase of sliding velocity,the friction co

关 键 词：非硫磷有机钼 低黏度润滑油 基底 减摩 抗磨 

分 类 号：TH117.1[机械工程—机械设计及理论] TG147[一般工业技术—材料科学与工程]