新型防老剂H37的制备及其在半钢子午线轮胎胎侧胶中的应用  

Preparation of New Antioxidant H37 and Its Application in Sidewall Compound of Steel-belted Radial Tire

作　　者：李剑波 王文博 杜孟成 马德龙 赵振伟 张浩 李云峰 LI Jianbo;WANG Wenbo;DU Mengcheng;MA Delong;ZHAO Zhenwei;ZHANG Hao;LI Yunfeng(National Engineering Technology Research Center for Rubber Chemical,Yanggu 252300,China)

机构地区：[1]国家橡胶助剂工程技术研究中心,山东阳谷252300

出　　处：《轮胎工业》2023年第1期39-42,共4页Tire Industry

摘　　要：研究新型防老剂H37的制备及其在半钢子午线轮胎胎侧胶中的应用。结果表明:与防老剂4020胶料相比,防老剂H37胶料的门尼焦烧时间延长,硫化速度加快,物理性能相当;在动态臭氧环境下,防老剂H37的耐变色性能优于防老剂4020,但抗龟裂性能差;在静态臭氧环境下,防老剂H37的耐变色性能优于防老剂4020,两种防老剂的抗龟裂性能相当;当防老剂H37/4020用量比为2/1时,可避免防老剂4020变色严重和防老剂H37抗龟裂性能差的问题。The preparation of new antioxidant H37 and its application in the sidewall compound of steelbelted radial tire were studied.The results showed that compared with the compound with antioxidant 4020,the Mooney scorch time of the compound with antioxidant H37 was extended,the curing speed was faster and the physical properties were similar.Under the dynamic ozone environment,the anti tarnish property of antioxidant H37 was better than that of antioxidant 4020,but the anti cracking property was poor.Under static ozone environment,the anti tarnish property of antioxidant H37 was better than that of antioxidant 4020,and the anti cracking property of the two antioxidants were equivalent.When the dosage ratio of antioxidant H37/4020 was 2/1,the problem of severe discoloration caused by antioxidant 4020 and poor anti cracking property with antioxidant H37 could be avoided.

关 键 词：防老剂 半钢子午线轮胎 胎侧胶 耐臭氧老化性能 

分 类 号：TQ330.382[化学工程—橡胶工业] U463.341.6[机械工程—车辆工程]