Modeling flow stress and grain size of GCr15 bearing steel at hightemperature deformation near end of solidification  

作　　者：Rui-hao Li Hai-jun Li Ning Xiang Guo-dong Wang Li-juan Bai 

机构地区：[1]The State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,Liaoning,China [2]HBIS Group Technology Research Institute,Shijiazhuang 050000,Hebei,China

出　　处：《Journal of Iron and Steel Research International》2023年第1期88-101,共14页

摘　　要：Hot-core heavy reduction rolling is an innovative technology for continuous casting billet at the end of solidification.The deformation characteristics of GCr15 bearing billet were investigated over the temperature range of 1000-1300℃ with the strain rate of 0.001-10 s^(-1) by the Gleeble 3800 thermo-mechanical simulator.Firstly,the true stress-strain data are calibrated by the friction correction method to acquire accurate parameters near the solidus.Then,the Laasraoui-type constitutive model and dynamic austenite grain size model are established by the thermal compression results and corrosion experimental results,and the predicted values of the experimental interval are obtained by using the models.Meanwhile,the accuracy of models is verified by comparing the predicted curves with the experimental data.Last but not the least,the dynamic parameters between solidus and liquidus are predicted by the two models,and the difficulty of experimental collecting near the melting point is solved.

关 键 词：Hot-core heavy reduction rolling High-temperature deformation GCr15 bearing billet Dynamic recrystallization Dynamic grain model 

分 类 号：TG142[一般工业技术—材料科学与工程]