Effect of oxygen addition and annealing time on microstructure and mechanical properties of Ti-34Nb alloy  

作　　者：Jun-shuai Wang Wen-long Xiao Lei Ren Yu Fu Chao-li Ma 

机构地区：[1]Key Laboratory of Aerospace Advanced Materials and Performance of Ministry of Education,School of Materials Science and Engineering,Beihang University,Beijing 100191,China

出　　处：《Journal of Iron and Steel Research International》2023年第1期158-164,共7页

基　　金：supported by the National Natural Science Foundation of China (No.51671012);the China Postdoctoral Science Foundation (2019TQ0015).

摘　　要：The effect of oxygen addition and annealing time on microstructure and mechanical properties of Ti-34Nb and Ti-34Nb-0.2O alloys was investigated.The addition of O suppresses the martensitic transformation.The phase composition changes from singleα''phase toα''+βphases with oxygen addition.The addition of oxygen increases strength significantly at as-received,cold-rolled,and annealed alloys through solid solution strengthening.The accumulation of abundance of defects and grain refinement introduced by cold rolling have a significant strengthening effect but also damage plasticity.The addition of oxygen increasesα/βtransformation temperature and promotes the precipitation ofαphase during annealing in Ti-34Nb-0.2O alloy.αprecipitates can inhibit grain growth during annealing.The strength decreases with annealing time increased due to the increase in grain size in Ti-34Nb alloy,while the strength increases in Ti-34Nb-0.2O alloy mainly due to the precipitation ofαphase.The cold rolling followed by annealing and addition of oxygen can improve the properties of alloys.

关 键 词：Titanium alloy Oxygen addition Annealing time αprecipitate 

分 类 号：TG146[一般工业技术—材料科学与工程]