富氧燃烧气氛下钢坯氧化烧损影响因素试验研究  

Experimental Study on Factors Affecting Oxidation Burning Loss of Billets in the Atmosphere of Oxygen Enriched Combustion

作　　者：赵俣 马光宇 张天赋 于庆波 包宇 吴彬 ZHAO Yu;MA Guangyu;ZHANG Tianfu;YU Qingbo;BAO Yu;WU Bin(State Key Laboratory of Metal Material for Marine Equipment and Application,Anshan 114009,Liaoning,China;Ansteel Iron&Steel Research Institutes,Anshan 114009,Liaoning,China;School of Metallurgy,Northeastern University,Shenyang 110819,Liaoning,China)

机构地区：[1]海洋装备用金属材料及其应用国家重点实验室,辽宁鞍山114009 [2]鞍钢集团钢铁研究院,辽宁鞍山114009 [3]东北大学冶金学院,辽宁沈阳110819

出　　处：《鞍钢技术》2023年第2期42-46,共5页Angang Technology

摘　　要：通过恒温动力学试验,模拟富氧燃烧气氛,研究不同工况对钢坯氧化烧损的影响。得出结论,钢坯表面温度和助燃空气富氧浓度越高,钢坯氧化烧损越严重;烟气中H_(2)O含量是影响钢坯氧化烧损的主要因素。Based on carrying out the simulation of the oxygen enriched combustion atmosphere by doing constant temperature kinetic test,the effect of different operation conditions on the oxidation burning loss of billets was studied.Then it was concluded that the higher the surface temperatures of billets and oxygen concentration of combustion-supporting air,the more severe the oxidation burning loss of the billets,while the content of H_(2)O in flue gas was the main cause affecting the oxidation burning loss.

关 键 词：富氧燃烧 钢坯 氧化烧损 恒温动力学试验 

分 类 号：TG307[金属学及工艺—金属压力加工]