不锈钢冷轧带钢卷取边浪成因分析及改善措施  

Cause Analysis and Improvement Measures of Coiling Edge Wave of Stainless Steel

作　　者：兰俊杰 Lan Junjie(Cold Rolling Plant of TISCO,Taiyuan Shanxi 030000)

机构地区：[1]山西太钢不锈钢股份有限公司冷轧厂,山西太原030000

出　　处：《山西冶金》2023年第2期112-114,共3页Shanxi Metallurgy

摘　　要：通过现场试验,确定了不锈钢精整过程中卷取边浪缺陷的形成原因。通过对比、分析横截面形状对原料板型缺陷的抵抗能力,找到一种对原料板型缺陷适应能力强、并且适用于不锈钢连轧机的带钢横截面。同时通过调整板型曲线和提供操作指导,使得实际生产中的带钢横截面与设计的横截面一致。Through the field test,the cause of the edge wave defect in the coiling process of stainless steel finishing was determined.By comparing and analyzing the resistance of cross section shape to raw material shape defects,a strip cross section with strong adaptability to raw material shape defects and suitable for stainless steel continuous rolling mill is found.At the same time,by adjusting the shape curve and providing operation guidance,the cross section of strip steel in actual production is consistent with the design cross section.

关 键 词：边浪 厚度 卷取缺陷 不锈钢 

分 类 号：TG335.6[金属学及工艺—金属压力加工]