Nanolignin,a Coupling Bio-Agent for Wood-Plastic Composites  

作　　者：Hamed Younesi-Kordkheili Antonio Pizzi 

机构地区：[1]Department of Wood and Paper Sciences,Faculty of Natural Resources,Semnan University,Semnan,Iran [2]LERMAB,University of Lorraine,Epinal,France

出　　处：《Journal of Renewable Materials》2023年第5期2075-2083,共9页可再生材料杂志（英文）

摘　　要：The influence of nanolignin coupling bio-agent on some characteristics of polypropylene-wood flour composites was studied.Thus,nanolignin was prepared by the acidic method,and then different ratios of it(0,1,3 and 5 wt%)were added to a polypropylene-wood flour mixture.After mechanically mixing wood flour,nanolignin,and polypropylene,the mixture was injection molded.ASTM methods were used to measure the structural properties of nanolignin,and prepared composites’water absorption,thickness swelling,bending modulus,and bending,tensile and impact strengths.Transforming the original lignin to nanolignin did not change the chemical bonds of the material.The addition of nanolignin yielded improved mechanical and physical properties of the composites prepared.Higher strength and dimensional stability are presented by nanolignin-containing composites when comparing them with those prepared with normal lignin.Nanolignin was shown by SEM(Scanning Electron Microscope)observation to be uniformly dispersed within the polymer matrix.Wood polymer composites(WPCs)with nanolignin exhibited comparable properties with the control samples prepared using maleic anhydride polypropylene(MAPP).

关 键 词：Coupling agent wood-plastic composite LIGNIN NANOPARTICLE 

分 类 号：TB333[一般工业技术—材料科学与工程]