Effects of Cationic Surfactant on Fresh and Hardened Properties of Cement-Based Mortar  

作　　者：Soumaya Zormati Fadhel Aloulou Habib Sammouda 

机构地区：[1]Laboratory of Energy and Materials,LabEM-LR11ES34,University of Sousse,Sousse,Tunisia

出　　处：《Journal of Renewable Materials》2023年第5期2345-2365,共21页可再生材料杂志（英文）

摘　　要：The objective of this study is to analyze the effects of using surfactant(CTAB)and cellulose nanofibers(NFC)as an admixture in cement mortars.We examined composite properties as porosity,compression energy,thermal conductivity and hydration.The results showed that with the addition of 0.7%by weight of NFC per emulsion in the presence of a cationic surfactant(CTAB).The new material produced presented a dry porosity between 4.7%and 4.4%,compressive strength between 9.8 and 22.9 MPa,and thermal conductivity between 0.95 and 2.25 W·m^(−1)·K^(−1).Thus we show better mechanical and thermal performance than that traditional Portland cement mortar with a density similar.In addition,the mortar made by emulsion of ordinary portland cement,cellulose nanofiber and organophilic clay(OC)treated with cetyltrimethylammonium bromide(CTAB)obtained has good resistance under high temperature and water,as well as excellent thermal insulation performance under high temperature and humidity conditions.This study verified that the presence of NFC promotes hydration,leading to the production of more calcium silicate and portlandite gel.

关 键 词：Cement nanofiber cellulose organophile-clay thermal conductivity hydration surfactant compressive strength MORTAR 

分 类 号：TQ172.1[化学工程—水泥工业]