焦磷酸哌嗪协同次磷酸铝阻燃聚丙烯复合材料性能  

Properties of Polypropylene Composites Flame Retarded by Piperazine Pyrophosphate and Aluminum Hypophosphite

作　　者：马殿普 郎丽君 潘飞 袁英杰 李俊 覃德清 吴景卿 符泽卫 彭巨擘 Ma Dianpu;Lang Lijun;Pan Fei;Yuan Yingjie;Li Jun;Qin Deqing;Wu Jingqing;Fu Zewei;Peng Jubo(Yunnan Tin Industry Group(Holding)Company Limted R&D Center,Kunming 650200)

机构地区：[1]云南锡业集团(控股)有限责任公司研发中心,昆明650200

出　　处：《工程塑料应用》2023年第4期133-138,共6页Engineering Plastics Application

基　　金：云南省重大科技专项(202102AB080002);云南省科技厅-云锡企业基础研究应用基础研究联合专项(202101BC70001-027);云南省“万人计划”产业技术领军人才专项(No.YNWR-CYJS-2017-056)。

摘　　要：为提高聚丙烯(PP)的阻燃性能,以焦磷酸哌嗪(PAPP)和次磷酸铝(AHP)为原料,通过熔融挤出的方式制备了不同质量比的PP复合材料,采用极限氧指数(LOI)、UL94垂直燃烧、热重分析(TG-DTG)、锥形量热(CONE)和扫描电子显微镜(SEM)等测试手段对PP复合材料热稳定性及阻燃抑烟性能进行分析,研究PAPP和AHP不同配比对阻燃性能的影响。结果表明,PAPP和AHP膨胀阻燃剂的加入大幅提升了PP复合材料的阻燃抑烟性能,当PAPP和AHP质量比为4∶1,总添加量为25%时,PP复合材料LOI达到31.5%,通过UL94垂直燃烧V-0级,800℃残炭率为23.16%,说明PAPP和AHP两者发挥了较好的协同阻燃作用。此外,其热释放速率(HRR)、总热释放量(THR)、烟释放速率(SPR)和总烟释放量(TSP)都得到大幅降低,SEM结果表明阻燃成分在PP复合材料表面形成了连续、致密的膨胀炭层,提升了材料的阻燃和抑烟性能。To improve the flame retardant properties of polypropylene(PP),PP composites with different mass ratios were prepared by melt extrusion with piperazine pyrophosphate(PAPP)and aluminum hypophosphate(AHP)as raw materials.The thermal stability,flame retardancy and smoke suppression properties of PP composites were analyzed by limiting oxygen index(LOI),UL94 vertical combustion,thermogravimetric analysis(TG-DTG),cone calorimetry(CONE)and scanning electron microscopy(SEM).The effect of different ratios of PAPP and AHP on flame retardancy was studied.The results showed that the addition of PAPP and AHP intumescent flame retardant significantly improved the flame retardancy and smoke suppression performance of PP composite.When the mass ratio of PAPP and AHP was 4:1 and the total addition was 25%,the LOI of PP composite reached 31.5%,and the carbon residue rate at 800℃was 23.16%after UL94 vertical combustion V-0,it shows that PAPP and AHP play a good synergistic flame retardant role.In addition,its heat release rate(HRR),total heat release(THR),smoke release rate(SPR)and total smoke release(TSP)were significantly reduced.The SEM results showed that the flame retardant components formed a continuous and dense expanded carbon layer on the surface of the PP composite,which improved the flame retardancy and smoke suppression properties of the material.

关 键 词：次磷酸铝 焦磷酸哌嗪 膨胀阻燃剂 协效剂 聚丙烯 