热处理工艺对近α高温钛基复合材料锻件组织性能的影响  

Effect of heat treatment on the microstructure and properties of TiBw reinforced high-temperature titanium matrix composite

作　　者：杨栋杰[1] 杨振博 孙永刚 冯弘 张树志[2] 智少勇 张长江[2] Yang Dongjie;Yang Zhenbo;Sun Yonggang;Feng Hong;Zhang Shuzhi;Zhi Shaoyong;Zhang Changjiang(Department of Materials Engineering,Shanxi Institute of Mechanical&Electrical Engineering,Changzhi 046011,Shanxi,China;College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,Shanxi,China;Shanxi Zhonggong Heavy Forging Co.Ltd.,Xinzhou 035400,Shanxi,China)

机构地区：[1]山西机电职业技术学院材料工程系,山西长治046011 [2]太原理工大学材料科学与工程学院,山西太原030024 [3]山西中工重型锻压有限公司,山西忻州035400

出　　处：《钢铁钒钛》2023年第1期72-77,共6页Iron Steel Vanadium Titanium

基　　金：山西省教育科学“十三五”规划课题项目(GH-19228)。

摘　　要：采用扫描电镜、电子万能材料试验机研究了整体锻造成形的TiBw增强高温钛基复合材料锻件的组织和性能,以及不同热处理工艺对锻件组织和性能的影响。结果表明:锻件组织为双态组织,在650℃时表现出优异的高温性能,但在700℃时其强度出现了大幅下降。对锻件进行了不同的热处理,发现随着固溶温度的升高,α相含量和尺寸逐渐降低。另外,其拉伸强度随着固溶温度的升高而升高,但其塑性则会降低。当固溶温度为1030℃时,可以得到等轴α相含量为18.58%的双态组织,此时高温性能最为优异。其屈服强度为514.0 MPa,极限抗拉强度最高为594.0 MPa,延伸率为13.9%。The microstructure and properties of TiBw reinforced high-temperature titanium matrix composite forgings formed by integral forging and the effects of different heat treatment processes on the microstructure and properties of forgings were studied by scanning electron microscope and electronic universal material testing machine. The results show that the microstructure of the forgings is bimodal structure, which shows excellent high-temperature performance at 650 ℃, but its strength decreases significantly at 700 ℃. Different heat treatments were performed on the forgings, and it was found that the content and size of the α phase gradually decreased with the increase of the solution temperature. In addition, its tensile strength increases with increasing solid solution temperature, but its plasticity decreases. When the solid solution temperature is 1 030 ℃, a bimodal structure with an equiaxed α-phase content of 18.58% can be obtained, and the high-temperature performance is the best. The yield strength is 514.0 MPa, the ultimate tensile strength is 594.0 MPa, and the elongation is 13.9%.

关 键 词：TiBw增强高温钛基复合材料 固溶温度 微观组织 力学性能 

分 类 号：TF823[冶金工程—有色金属冶金]