Sol-gel-based porous Ti-doped tungsten oxide films for high-performance dual-band electrochromic smart windows  

作　　者：Qiancheng Meng Sheng Cao Juquan Guo Qingke Wang Ke Wang Tao Yang Ruosheng Zeng Jialong Zhao Bingsuo Zou 

机构地区：[1]School of Physical Science and Technology,MOE Key Laboratory of New Processing Technology for Non-ferrous Metals and Materials,Guangxi University,Nanning 530004,Guangxi,China [2]Beijing Advanced Innovation Center for Materials Genome Engineering,University of Science and Technology Beijing,Beijing 100083,China

出　　处：《Journal of Energy Chemistry》2023年第2期137-143,I0004,共8页能源化学（英文版）

基　　金：supported by the National Natural Science Foundation of China(51902064);the Natural Science Foundation of Guangxi(2022GXNSFFA0350325);the Scientific and Technological Bases and Talents of Guangxi(Guike AD20159073);the special fund for“Guangxi Bagui Scholars”;the“Guangxi HundredTalent Program”。

摘　　要：Dual-band electrochromic smart windows(DESWs)with independent control of the transmittance of near-infrared and visible light show great potential in the application of smart and energy-saving buildings.The current strategy for building DESWs is to screen materials for composite or prepare plasmonic nanocrystal films.These rigorous preparation processes seriously limit the further development of DESWs.Herein,we report a facile and effective sol-gel strategy using a foaming agent to achieve porous Ti-doped tungsten oxide film for the high performance of DESWs.The introduction of foaming agent polyvinylpyrrolidone during the film preparation can increase the specific surface area and free carrier concentration of the films and enhance their independent regulation ability of near-infrared electrochromism.As a result,the optimal film shows excellent dual-band electrochromic properties,including high optical modulation(84.9%at 633 nm and 90.3%at 1200 nm),high coloration efficiency(114.9 cm^(2) C^(-1) at 633 nm and 420.3 cm^(2) C^(-1) at 1200 nm),quick switching time,excellent bistability,and good cycle stability(the transmittance modulation losses at 633 and 1200 nm were 11%and 3.5%respectively after 1000 cycles).A demonstrated DESW fabricated by the sol-gel film showed effective management of heat and light of sunlight.This study represents a significant advance in the preparation of dual-band electrochromic films,which will shed new light on advancing electrochromic technology for future energy-saving smart buildings.

关 键 词：ELECTROCHROMISM Tungsten oxide Smart windows Sol-gel method Dual-band absorption 

分 类 号：TU855[建筑科学] TB383.2[一般工业技术—材料科学与工程]