超细铜尾矿免烧免蒸养环保砖的研究  

Research on Ultrafine Copper Tailings Free of Burning and Free of Steamboat Environmental Bricks

作　　者：王红英 黄高明 刘红霞 刘澜涛 刘文杰 Wang Hongying;Huang Gaoming;Liu Hongxia;Liu Lantao;Liu Wenjie(Jiangxi Building Materials Research and Design Institute Co.Ltd.,Nanchang,Jiangxi 330001)

机构地区：[1]江西省建材科研设计院有限公司,江西南昌330001

出　　处：《江西建材》2023年第1期18-21,共4页Jiangxi Building Materials

摘　　要：文中通过正交试验得出适用于超细铜尾矿的最佳固化剂配方为:水泥、粉煤灰、消石灰、脱硫石膏和石英粉用量分别为25%、40%、25%、4%和6%。固化剂掺量为20%时,超细铜尾矿免烧免蒸养环保砖的性能最佳,其7d、28d抗压强度分别为17.6MPa、22.5MPa,软化系数分别为0.65和0.80。C-S-H凝胶、钙矾石[Ca_(6)Al_(2)(SO_(4))_(3)(OH)_(12)·26H_(2)O]等新矿物的生成是超细铜尾矿环保砖具有较高的抗压强度和耐水性的主要原因。In this study,the optimal ratio of curing agent suitable for ultrafine copper tailings is that the dosage of cement,fly ash,hydrated lime,desulfurized gypsum and limestone powder are 25%,40%,25%,4% and 6% respectively.When the mixing amount of curing agent is 20%,the performance of environmental brick is best,with the compressive strength of 7d and 28d are 17.6,22.5 MPa respectively,and the softening coefficient are 0.65 and 0.80 respectively.The generation of new minerals such as C-S-H gel and CagAl,(SO_(4))_(3)(OH)_(12)·26H_(2)O is the main reason for the high compressive strength and water resistance of ultrafine copper tailings environmental brick.

关 键 词：固化剂 超细铜尾矿环保砖 抗压强度 软化系数 

分 类 号：TU522[建筑科学—建筑技术科学]