High ceramic content composite solid-state electrolyte films prepared via a scalable solvent-free process  

作　　者：Daiqian Chen Chenji Hu Qi Chen Guoyong Xue Lingfei Tang Qingyu Dong Bowen Chen Fengrui Zhang Mingwen Gao Jingjing Xu Yanbin Shen Liwei Chen 

机构地区：[1]School of Physical Science and Technology,ShanghaiTech University,Shanghai 201210,China [2]i-Lab,CAS Center for Excellence in Nanoscience,Suzhou Institute of Nano-Tech and Nano-Bionics(SINANO),Chinese Academy of Sciences,Suzhou 215123,China [3]School of Chemistry and Chemical Engineering,Frontiers Science Center for Transformative Molecules,and in situ Center for Physical Sciences,Shanghai Jiao Tong University,Shanghai 200240,China [4]Baosheng(Suzhou)Energy Technology Co.,Ltd,Suzhou 215123,China

出　　处：《Nano Research》2023年第3期3847-3854,共8页纳米研究（英文版）

基　　金：supported by the National Natural Science Foundation of China(Nos.21733012 and 22179143);the National Key R&D Program of China(No.2021YFB3800300).

摘　　要：The development of high-performance solid-state electrolyte(SSE)films is critical to the practical application of all-solid-state Li metal batteries(ASSLMBs).However,developing high-performance free-standing electrolyte films remains a challenging task.In this work,we demonstrate a novel scalable solvent-free process for fabricating high ceramic content composite solid-state electrolyte(HCCSE)films.Specifically speaking,a mixture of ceramic and polymer is dry mixed,fibered,and calendered into a free-standing porous ceramic film,on which polymer precursor is coated and polymerized to bridge the inorganic ceramic particles,resulting in a flexible HCCSE film with a ceramic content of up to 80 wt.%.High ceramic content not only leads to high ionic conductivity but also brings good mechanical properties;while the organic phase enables electrode|electrolyte interfacial stability.When Li_(10)GeP_(2)S_(12)(LGPS)and polymeric ionic liquid-based solid polymer electrolytes(PIL-SPEs)were used as the inorganic and organic phases,respectively,the room temperature ionic conductivity of the resulted HCCSE reaches 0.91 mS·cm−1.Based on this HCCSE,Li||Li symmetric battery cycled stably for more than 2,400 h with ultra-low overpotential,and ASSLMBs with different cathodes(LiFePO4 and sulfurized polyacrylonitrile(PAN-S))present small polarization and decent cyclability at room temperature.This work provides a novel scalable solvent-free strategy for preparing high-performance freestanding composite solid-state electrolyte(CSE)film for room temperature ASSLMBs.

关 键 词：FREE-STANDING solid-state electrolyte film composite solid-state electrolyte solid-state battery 

分 类 号：TM912[电气工程—电力电子与电力传动]