结构设计对传动带用浸胶芳纶线绳性能的影响  

Effect of Structure Design on Properties of Dipped Aramid Cord for Transmission Belt

作　　者：于得江 吴贻珍 施骏捷 高渭淞 姜伟 YU Dejiang;WU Yizhen;SHI Junjie;GAO Weisong;JIANG Wei(Qingdao Tipont Cord Co.,Ltd,Qingdao 266609,China;Wuxi Rubber Belt Co.,Ltd,Wuxi 214176,China;DuPont(China)R&D and Management Co.,Ltd,Shanghai 201203,China)

机构地区：[1]青岛天邦线业有限公司,山东青岛266609 [2]无锡市贝尔特胶带有限公司,江苏无锡214176 [3]杜邦(中国)研发管理有限公司,上海201203

出　　处：《橡胶科技》2023年第5期235-239,共5页Rubber Science and Technology

摘　　要：分别采用1670dtex和1100dtex芳纶丝,研究结构设计对传动带用浸胶芳纶线绳性能的影响。结果表明:当原丝总纤度相同时,随着初复捻捻度的增大,捻度系数增大,线绳的初始断裂强力呈减小趋势,疲劳后断裂强力保持率呈增大趋势;当捻度相同时,增大原丝纤度,可提高线绳的耐疲劳性能;当直径和捻度相同时,通过改变捻线结构,增大初捻捻度系数,保持复捻捻度系数不变,可使线绳的耐疲劳性能得到提高。The effect of structure design on the properties of dipped aramid cords for transmission belts was studied by using 1670dtex and 1100dtex aramid yarn.The results showed that when the total filament size was the same,with the increase of the initial and secondary twist,the twist coefficients increased,the initial breaking strength of the cord decreased and the breaking strength retention rate after fatigue increased.When the twist was the same,the fatigue resistance of the cord could be improved by increasing the filament size.When the diameter and twist were the same,the fatigue resistance of the cord could be improved by changing the twist structure,increasing the initial twist coefficient,and keeping the secondary twist coefficient unchanged.

关 键 词：传动带 芳纶纤维 捻度系数 耐疲劳性能 断裂强力 

分 类 号：TQ336.2[化学工程—橡胶工业] TQ330.389