Effect of annealing time on microstructure and mechanical properties of cryorolled AISI 310S stainless steel  

作　　者：Xue-kui Lian Yong Li Yi Xiong Yong-li Wu Shun Han Tian-tian He Chun-xu Wang Feng-zhang Ren 

机构地区：[1]Central Iron and Steel Research Institute Co.,Ltd.,Beijing 100081,China [2]School of Materials Science and Engineering,Henan University of Science and Technology,Luoyang 471023,Henan,China [3]Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology,Luoyang 471023,Henan,China

出　　处：《Journal of Iron and Steel Research International》2023年第3期548-556,共9页

基　　金：This work was supported by the National Natural Science Foundation of China(Grant Nos.U1804146,52111530068 and 51905153);the Science and Technology Innovation Team of Henan University of Science and Technology(Grant No.2015XTD006);the Foreign Experts Introduction Project of Henan Province(Grant No.HNGD2020009).

摘　　要：AISI 310S stable austenitic stainless steel was subjected to 90%cryorolling and then annealed at 800 ℃ for 2-60 min.The effect of annealing time on the microstructure and mechanical properties was studied by optical microscopy,scanning electron microscopy,transmission electron microscopy,microhardness and tensile test.The results show that the grain size of AISI 310S stainless steel is refined to the nanometer level after 90%cryorolling,and the grain size is approximately 20 nm.With the increase in annealing time,the degree of grain recrystallization occurs more fully and completely,as the grain begins to grow and then tends to stabilize.The strength and hardness of the annealed specimens decrease with increasing annealing time,while elongation tends to increase.When the annealing time is 10 min,the yield strength increases by about 2 times compared to that of the original austenite(unrolled),and the elongation is also above 20%,which is the best preparation process for ultra-fine grain austenitic stainless steel under this experimental condition.As the annealing time treatment increases,the fracture morphology changes from mixed quasi-cleavage and ductile fracture(after cryorolling)to ductile fracture(after annealing).

关 键 词：Austenitic stainless steel CRYOROLLING Annealing time MICROSTRUCTURE Mechanical property 

分 类 号：TG142.71[一般工业技术—材料科学与工程]