单分散聚苯乙烯和聚(苯乙烯-co-苯乙烯磺酸钠)乳胶粒的制备及其喷墨流畅性  

Preparation and inkjet printing smoothness of monodisperse polystyrene and poly(styrene-co-styrene sulfonate)latex particles

作　　者：苏婧 关玉 付少海[1,2,3] SU Jing;GUAN Yu;FU Shaohai(College of Textile Science and Engineering,Jiangnan University,Wuxi,Jiangsu 214122,China;Key Laboratory of Eco-Textiles(Jiangnan University),Ministry of Education,Wuxi,Jiangsu 214122,China;National Innovation Center of Advanced Dyeing and Finishing Technology,Taian,Shandong 271000,China)

机构地区：[1]江南大学纺织科学与工程学院,江苏无锡214122 [2]生态纺织教育部重点实验室(江南大学),江苏无锡214122 [3]国家先进印染技术创新中心,山东泰安271000

出　　处：《纺织学报》2023年第5期13-20,共8页Journal of Textile Research

基　　金：国家自然科学基金项目(22278185);国家先进印染技术创新中心科研基金项目(ZJ2021A08)。

摘　　要：为探究颜料墨水中固体颗粒粒径与喷墨流畅性之间的关系,制备了不同粒径的单分散球形聚苯乙烯(PSt)和聚(苯乙烯-co-苯乙烯磺酸钠)(P(St-co-SS))乳胶粒,探究了乳胶粒大小与分散液储存稳定性和喷墨流畅性的关系,并结合有限元与密度泛函计算,从理论角度解释乳胶粒大小与电荷对其喷墨流畅性的影响。结果表明:通过控制引发剂、乳化剂或水溶性单体的加入量,成功制备不同粒径的单分散球形PSt和P(St-co-SS)乳胶粒;固含量为10%的PSt和P(St-co-SS)乳胶粒分散液在4~50℃温度范围内储存4个月后分散稳定性均大于96%;随着分散液中乳胶粒粒径的增大,分散液的抽滤流速逐渐降低,且相同粒径下P(St-co-SS)较PSt分散体系的抽滤流速更高;粒孔比的增大会导致分散液在孔道内的流动体积降低,最终造成滤孔的堵塞,而微粒上表面活性剂的脱吸附是造成相同粒径下PSt体系抽滤流畅性低于P(St-co-SS)体系的原因。Objective The smoothness of digital inkjet printing depends on the pigment ink′s particle size,but at the moment,research on the relationship between particle size and flow primarily focuses on the suspension system of large particles,and the choice of pigment ink particle size is largely determined by engineering expertise.Consequently,it is crucial to develop a realistic particle size range appropriate for inkjet.However,most convenitional pigments are prepared by grinding or other physical methods,and their size and morphology distribution is relatively random,making quantitative research impossible.Method As a new polymer,latex particle size is easy to control and the performance is stable,making it a suitable choice for the study of particle size and inkjet fluidity.Monodisperse spherical polystyrene(PSt)and poly(styrene-co-styrene sulfonate)(P(St-co-SS))latex particles of different sizes were prepared by mini-emulsion polymerization and soap-free emulsion polymerization,respectively,which were configured into PSt latex particle dispersions and P(St-co-SS)latex particle dispersions.The relationships among latex particle size,storage stability and inkjet fluidity of the dispersions were investigated.Results In this research,monodisperse spherical PSt and P(St-co-SS)latex particles with controllable particle size of 50-250 nm were successfully prepared by changing the addition of potassium persulfate(KPS),sodium dodecyl sulfate(SDS)and sodium p-styrene sulfonate(SS)in the reaction components.The prepared latex particles were uniform in size and had a spherical structure(Fig.2).The results of storage stability tests suggested the temperature range of 4-50℃for PSt latex particle dispersion and P(St-co-SS)latex particle dispersion,respectively(Fig.4).It was seen that the storage stability of both PSt and P(St-co-SS)latex particle dispersions was higher than 96%in this temperature range,and that the smaller the particle size of latex particles,the better the storage stability of the dispersions.Subsequently,th

关 键 词：聚苯乙烯 聚(苯乙烯-co-苯乙烯磺酸钠) 乳胶粒 喷墨流畅性 单分散体系 颜料墨水 喷墨印花 