Quality Improvement of Recycled Concrete Aggregate by Accelerated Carbonation under Different Pressure  

作　　者：丁亚红 武军 ZHANG Xianggang XU Ping NING Wei LI Yajing DING Yahong;WU Jun;ZHANG Xianggang;XU Ping;NING Wei;LI Yajing(School of Civil Engineering,Henan Polytechnic University,Jiaozuo 454003,China;School of Civil Engineering and Architecture,XinxiangUniversity,Xinxiang453003,China)

机构地区：[1]School of Civil Engineering,Henan Polytechnic University,Jiaozuo 454003,China [2]School of Civil Engineering and Architecture,XinxiangUniversity,Xinxiang453003,China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2023年第3期623-631,共9页武汉理工大学学报（材料科学英文版）

基　　金：Funded by Joint Funds of the National Natural Science Foundation of China (No.U1904188);Key R&D and Promotion Projects in Henan Province,China (No.212102310288);the Key Science and Technology Program of Henan Province,China (No.202102310253)。

摘　　要：Due to the presence of old mortar (OM) and interfacial transition zone (ITZ),recycled concrete aggregate (RCA) is inferior to natural aggregate (NA).The purpose of this paper was to study the effect of accelerated carbonation on the macro-properties and micro-properties of RCA under different pressure(0.05,0.15,0.30 MPa).The macro-property tests included colour change,apparent density,water absorption,and crushing value of RCA.The micro-property tests included scanning electron microscopy (SEM),X-ray diffraction (XRD),thermogravimetry-differential scanning calorimetry (TG-DSC),and Vickers micro-hardness(VMH).The results showed that the change trends of apparent density,water absorption,and crushing value of RCA displayed exponential relationships as pressure increasing,with the optimum pressure of 0.30 MPa.SEM images indicated that the calcite caused by the hydration products in RCA and the Ca(OH)_(2) derived from saturated lime water improved the properties of RCA;as the apparent density increased,the water absorption and crushing value decreased.The results of XRD and TG-DSC indicated that,as the pressure increased,the masses of Ca(OH)_(2) in carbonated RCA gradually decreased,while those of CaCO_(3) gradually increased,which demonstrated that the carbonation degree gradually increased.Besides,ITZ-2 was the weakest phase in RCA,but its improvement degree of VMH by accelerated carbonation was higher than that of OM.However,RCA was not completely carbonated,but only carbonated in a certain depth after 24 h accelerated carbonation.

关 键 词：recycled concrete aggregate treatment method accelerated carbonation interfacial transition zone saturated lime water CALCITE 

分 类 号：TU528.041[建筑科学—建筑技术科学]