易染间位芳纶的制备及其性能  

Preparation and properties of dyeable meta-aramid fiber

作　　者：关振虹 李丹 宋金苓 冷向阳 宋西全 GUAN Zhenhong;LI Dan;SONG Jinling;LENG Xiangyang;SONG Xiquan(Yantai Tayho Institute of Novel Polymeric Materials Co.,Ltd.,Yantai,Shandong 264000,China;Yantai Tayho Advanced Materials Co.,Ltd.,Yantai,Shandong 264000,China)

机构地区：[1]烟台泰和新材高分子新材料研究院有限公司,山东烟台264000 [2]烟台泰和新材料股份有限公司,山东烟台264000

出　　处：《纺织学报》2023年第6期28-32,共5页Journal of Textile Research

摘　　要：为提升间位芳纶的染色效果,从分子结构改性出发,引入易染基团。采用溶液聚合法在聚合反应过程中加入4,4′-二氨基二苯砜(DDS),在聚间苯二甲酰间苯二胺分子结构中引入砜基,通过调整DDS的加入量调控聚合物分子结构中砜基的含量,采用湿法纺丝工艺制备改性间位芳纶。测试了改性间位芳纶及其织物的染色性能、力学性能、阻燃性能和色牢度。结果表明:随着DDS引入量的增加,改性间位芳纶的染色性能得到明显提升,当间苯二胺与DDS的量比为7∶3时,采用阳离子红染色后改性间位芳纶的K/S值为3.82,比常规间位芳纶提高1.39;采用阳离子蓝染色后改性间位芳纶的K/S值为5.83,比常规间位芳纶提高2.74,采用分散蓝、分散红对纤维染色也具有较好的染色效果。此外,改性间位芳纶织物保持良好的力学性能,其断裂强度为3.65 cN/dtex,断裂伸长率为35.21%;与常规间位芳纶织物相比,改性间位芳纶织物的力学性能和阻燃性能无明显变化,耐干湿摩色牢度和耐日晒色牢度提升1级。Objective The molecular chain structure of meta-aramid fiber is relatively regular,coupled with strong hydrogen bonding between the molecular chains,and it has excellent mechanical properties and comprehensive properties.Its disadvantages lie in its difficulty in dyeing due to its regular molecular structure,high crystallinity,high orientation and high glass transition temperature,which limits its further application.This research was carried out in order to improve the combination of meta-aramid fibers and dyes,improve their dyeing properties,and further expand the application of meta-aramid fibers in the field of post-dyeing.Method This research uses solution polymerization method to add the form of the third monomer in the polymerization process,introduce easy-dyeing groups into the molecular structure of polyphthaloyl-mphenylenediamine,adjust the number of easy-dyeing groups,and then adjust the molecular structure of the polymer to achieve the objective of easy dyeing.Results In this paper,4,4′-diaminophenyl sulfone(DDS)was selected as the third monomer,and the modified meta-aramid fiber was prepared by adjusting the content of sulfone group in the molecular chain.The results show that the dyeing property of modified meta-aramid fiber was significantly improved with the increased amount of DDS.When the molar ratio of m-phenylenediamine to DDS was set to 7∶3,the modified meta-aramid fiber maintained good mechanical properties,and the prepared modified meta-aramid fiber showed excellent dyeing property(Tab.1).After that,the dyeing properties of modified meta-aramid fiber,conventional meta-aramid fiber and imported XJ easily dyed meta-aramid fiber products were analyzed.The K/S value of the modified meta-aramid fiber prepared in this research using Cationic Red FBL dye was 3.82,1.39 higher than that of conventional metaaramid fiber.The K/S value of Cationic Blue FGGL dye was 5.83,which is 2.74 higher than that of conventional meta-aramid fiber.The K/S value of modified meta-aramid fiber dyed with Disperse Re

关 键 词：溶液聚合 湿法纺丝 间位芳纶 易染 染色性能 

分 类 号：TQ342.7[化学工程—化纤工业]