聚乳酸/聚3-羟基丁酸-戊酸酯共混纤维及其雪尼尔纱的染色动力学  

Dyeing kinetics of polylactide/poly(3-hydroxybutyrate-co-valerate)blended fibers and their chenille yarns

作　　者：唐奇 柴丽琴 徐天伟 王成龙[1] 王直成 郑今欢[1] TANG Qi;CHAI Liqin;XU Tianwei;WANG Chenglong;WANG Zhicheng;ZHENG Jinhuan(Engineering Research Center for Eco-Dyeing and Finishing of Textiles,Ministry of Education,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China;Huzhou Beiheng Textile Co.,Ltd.,Huzhou,Zhejiang 313021,China)

机构地区：[1]浙江理工大学生态染整技术教育部工程研究中心,浙江杭州310018 [2]湖州倍亨纺织有限公司,浙江湖州313021

出　　处：《纺织学报》2023年第6期129-136,共8页Journal of Textile Research

基　　金：浙江省基础公益研究计划项目(LGC20E030001,LGF21E030004)。

摘　　要：为进一步了解生物可降解聚乳酸/聚3-羟基丁酸-戊酸酯(PLA/PHBV)共混纤维及其雪尼尔纱的染色性能,提高对含生物可降解聚酯纤维雪尼尔纱染色技术的可控性,研究了PLA/PHBV纤维及PET/(PLA/PHBV)雪尼尔纱的染色性能,探究了C.I.分散红60在雪尼尔纱及其原材料纤维上的染色动力学,并对各纤维的生物可降解性能进行了研究。结果表明:C.I.分散红60在PLA/PHBV纤维及PET/(PLA/PHBV)雪尼尔纱上的上染率随着温度的升高而明显提升,但为兼顾纤维的力学性能,染色温度不宜超过110℃;C.I.分散红60在PET纤维、PLA/PHBV纤维及雪尼尔纱3种材料上的吸附均符合准二级动力学方程,其在PLA/PHBV纤维上的染色平衡吸附量最高,在PET纤维上的最低,并且随着染色温度升高,C.I.分散红60在3种材料上的染色速率加快,半染时间缩短,扩散系数增大;各纤维的降解效率均随土埋时间的延长而提高,其中PLA/PHBV纤维的降解性能最好,PLA纤维次之,且PLA或PLA/PHBV生物可降解聚酯纤维的存在,可加快PET纤维的降解速率。Objective In order to further understand the dyeing performance of biodegradable polylactide/poly(3-hydroxybutyrate-co-valerate)(PLA/PHBV)blended fibers and their chenille yarns,and to improve the controlled dyeing technology of chenille yarn containing biodegradable polyester fiber,dyeing research was carried out.Method The dyeing properties of PLA/PHBV fiber and PET/(PLA/PHBV)chenille yarn was studied and the parameters of dyeing rate constant,half dyeing time and diffusion coefficient were analyzed.Dyeing kinetics of C.I.Dispersed Red 60 on chenille yarn and its raw materials were explored and the biodegradable properties of each fiber were also studied.Results The research results show that dyeing rate of C.I.Dispersed Red 60 on PLA/PHBV fiber and PET/(PLA/PHBV)chenille yarn was increased obviously with the increase of temperature,but the dyeing temperature was found not to exceed 110℃in order to achieve the required mechanical properties of the fiber(Tab.1 and Fig.2).When the bath ratio was close to infinity,C.I.Dispersed Red 60 could stain the three materials faster at the initial stage of dyeing,after dyeing at 100℃for 50 min,the adsorption capacity of the fibers to dyes basically reached the equilibrium state(Fig.4(a)).When the dyeing temperature was increased to 110℃,the initial dyeing rate and equilibrium dyeing amount of C.I.Dispersed Red 60 on the three materials were significantly increased,and the time to reach the equilibrium state was shortened to about 40 min(Fig.4(b)).The adsorption of C.I.Dispersed Red 60 on PET,PLA/PHBV and chenille yarn conformed to the quasi-second-order kinetic equation(Fig.6).Among them,C.I.Dispersed Red 60 had the highest dyeing equilibrium adsorption capacity on PLA/PHBV fiber,and the lowest on PET fiber.With the increase of dyeing temperature,the dyeing rate of C.I.Disperse Red 60 on the three materials was accelerated(Tab.3),the half staining time was shortened and the diffusion coefficient was increased(Tab.4).The results of soil burial test showed that the degr

关 键 词：聚乳酸/聚3-羟基丁酸-戊酸酯共混纤维 雪尼尔纱 分散染料 染色性能 染色动力学 