15CrMoG矩形坯保护渣优化实践  

Optimization Practice of 15CrMoG Rectangular Billet Protection Slag

作　　者：张军卫 郝文权 颜昊 刘政鹏 Zhang Junwei;Hao Wenquan;Yan Hao;Liu Zhengpeng(Technology Research Institute of Qingdao Special Iron&Steel Co.,LTD.,Qingdao 266409,China)

机构地区：[1]青岛特殊钢铁有限公司工艺研究所,青岛266409

出　　处：《特殊钢》2023年第4期70-73,共4页Special Steel

摘　　要：针对15CrMoG矩形坯出现的凹陷与纵向裂纹,设计了保护渣熔化温度、碱度、粘度等技术参数。将保护渣碱度由0.85调整到1.15,熔点由1132℃调整到1200℃,粘度由0.67 Pa·s调整到1.4 Pa·s,提高保护渣的析晶率,增大固态渣膜厚度,提高热阻,均匀稳定了传热;同时将保护渣熔速由70 s优化到32 s,控制振动参数,提高非正弦振动偏斜率,增大保护渣消耗量,改善润滑。通过保护渣理化指标和振动参数的优化,消除了铸坯表面凹陷与纵向裂纹。不良铸坯的精整处理比例大幅降低,减少了铸坯修磨工作量,提高了金属收得率。Aiming at the sags and longitudinal cracks of 15CrMoG rectangular billet,the meling temperature,alkalinity,viscosity and other technical parameters of protective slag were designed.By adjusting the alkalinity of the protective slag from0.85 to 1.15,the melting point from 1132 Cto 1200 C,and the viscosity from 0.67 Pa'sto 1.4 Pa*s,the crystal-lization rate of the protective slag was increased,the thickness of solid-state slag film was increased,the thermal resis-tance was improved,and the heat transfer was uniformly stabilized.At the same time,the melting rate of the slag was opti-mized from 70s to 32 s,vibration parameters were controlled,non-sinusoidal vibration bias slope was increased,slag con-sumption was increased,and lubrication was improved.The surface sags and longitudinal cracks of the billet were elimi-nated by optimizing the physicochemical parameters and vibration parameters of the slag.The proportion of defective cast-ing billet finishing treatment was greatly reduced,which reduced the grinding work of casting billet and improved the metal.recovery rate.

关 键 词：15CrMoG钢 凹陷 纵裂 保护渣 

分 类 号：TF703[冶金工程—钢铁冶金]