16MnCr5高温热塑性及连续冷却转变曲线测定及应用  

Determination and Application of High Temperature Thermoplasticity and Continuous Cooling Transition(CCT)Curve of 16MnCr5

作　　者：王宁涛 王利军 郭俊成 韩光洋 Wang Ningtao;Wang Lijun;Guo Juncheng;Han Guangyang(Hebei Engineering Innovation Center for Wire Rod,Xingtai 054027,China;Technical Centre,Xingtai Iron&Steel Co.,Ltd.,Xingtai 054027,China;Wire Rod Plant of Xingtai Iron&Steel Co.,Ltd.,Xingtai 054027,China;Sales department of Xingtai Iron&Steel Co.,Ltd.,Xingtai 054027,China)

机构地区：[1]河北省线材工程技术创新中心,邢台054027 [2]邢台钢铁有限责任公司技术中心,邢台054027 [3]邢台钢铁有限责任公司线材厂,邢台054027 [4]邢台钢铁有限责任公司销售公司,邢台054027

出　　处：《特殊钢》2023年第4期120-124,共5页Special Steel

摘　　要：动态高温热塑性实验表明16MnCr5钢在第II脆性区(900~1200℃)未出现脆性,最佳变形温度为800~1050℃。在600~750℃之间塑性变差,对应于第Ⅲ脆性区。连续冷却转变实验表明16MnCr5钢在0.5~3℃/s之间冷却时,得到均匀的铁素体和珠光体组织;超过5℃/s冷却时,出现贝氏体组织。16MnCr5钢连铸坯冷却到600℃组织转变刚完成或尚未完成,因此,热装的温度应尽量低于600℃。16MnCr5钢盘条轧制后关闭保温罩缓冷,运用于生产Φ30 mm大规格16MnCr5钢线材,组织为F+P,晶粒度约7.5级,硬度达到80HRB,组织均匀,可以满足下游用户拉拔、冷镦使用要求。The dynamic high temperature ductility test shows that 16MnCr5 steel does not appear britleness in the second britle zone(900-1200℃),and the optimum deformation temperature is 800-1050℃.The plasticity decreases between 600and 750℃,corresponding to the third britle zone.The continuous cooling transfomation experiment shows that when 16MnCr5 steel is cooled at speed between 0.5-3℃/s,uniform ferrite and pearlite structure can be obtained;When the cooling speed is more than 5℃/s,bainite appears.The structure transformation of 16MnCr5 steel continuous casting billet cooled to 600℃has just been completed or has not yet been completed,therefore the temperature of hot charging should be lower than 600 C as far as posble.Afer16Mncr5 wirerod is roled,close the insulation cover for slow cooling which is conducive to subsequent processing.After rolling 16 MnCr5 steel wire rods,the insulation cover is closed for slow cooling,which is used in the production of 030 mm large size 16 MnCr5 steel wire rod.The microstructure is F+P with grain size about 7.5,hardness about 80HRB,and uniform microstructure,which can meet the requirements of down-stream customers for drawing and cold heading.

关 键 词：16MnCr5钢 高温热塑性 CCT 热装 

分 类 号：TG142.1[一般工业技术—材料科学与工程]