Novel bake hardening mechanism for bainite-strengthened complex phase steel  

作　　者：Hang Yu Yu Yan Cheng Zhang Lijie Qiao 

机构地区：[1]Beijing Advanced Innovation Center for Materials Genome Engineering,University of Science and Technology Beijing,Beijing 100083,China [2]Corrosion and Protection Center,University of Science and Technology Beijing,Beijing 100083,China

出　　处：《Journal of Materials Science & Technology》2023年第12期117-128,共12页材料科学技术（英文版）

基　　金：supported by the National Natural Science Foun-dation of China (No.U1964204).

摘　　要：In the automobile industry,stamping and paint baking processes are used to strengthen components,and this not only saves costs,but also further reduces the bodyweight of automobiles.In this work,the bake hardening mechanism of the complex phase(CP)steel CP980 was explored by comparing it with that of DP1180,which has a clear bake hardening mechanism and a carbon content similar to that of CP980.By analyzing the bake hardening response and the microstructural changes of the two steels,we found that the bake hardening process of CP980 was divided into three stages.In the first two stages,the carbon atoms diffused into dislocations to form Cottrell atmosphere pinning dislocations,and excess car-bon atoms formed carbon clusters or low-temperature carbide pinning dislocations that were similar to DP1180.In the third stage,the dislocation acted as rapid channels for carbon diffusion,and fine cementite gradually formed when the carbon clusters gathered at the dislocations as precursors,resulting in pre-cipitation hardening.This novel bake-hardening(BH)mechanism is crucial for obtaining a comprehensive understanding of the strain-baking behavior of advanced high-strength steals(AHSS).

关 键 词：Age hardening Bainitic steel Carbon diffusion CEMENTITE Mechanical property Automotive weight reduction 

分 类 号：TG113[金属学及工艺—物理冶金]