Fretting wear behavior of Zr alloy cladding tube mated with Zr alloy dimple under mixed fretting regime in simulated primary water of PWR  

作　　者：Yusheng Zhang Hongliang Ming Jiang Lai Lixia Gao Jianqiu Wang En-Hou Han 

机构地区：[1]CAS Key Laboratory of Nuclear Materials and Safety Assessment,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China [2]School of Materials Science and Engineering,University of Science and Technology of China,Shenyang 110016,China [3]Nuclear Power Institute of China,Chengdu 610213,China

出　　处：《Journal of Materials Science & Technology》2023年第27期43-52,共10页材料科学技术（英文版）

基　　金：financially supported by the CNNC Science Fund for Talented Young Scholars,the Youth Innovation Promotion As-sessment CAS(No.2022187);the National Natural Science Founda-tion of China(No.52105221);the IMR Innovation Fund(No.2021-PY10);the open-ended fund of the CAS Key Laboratory of Nu-clear Materials and Safety Assessment(Institute of Metal Research,Chinese Academy of Sciences,China)(No.2020NMSAKF01).

摘　　要：The fretting wear behavior of Zr alloy cladding tube under mixed fretting regime in a high-temperature pressurized water was investigated.The main wear mechanism is adhesive wear,with characters of small-scale delamination at the center of worn area and serious delamination on the worn edge.A long crack throughout the worn area and other cracks propagated towards the substrate are observed.The cross-sectional microstructure of worn area can be divided into a thick third-body layer,thin inner oxide layer and thick tribologically transformed structure layer,and their formation mechanisms are analyzed in detail.Finally,the mixed fretting regime process and the microstructural evolution during fretting wear are discussed.

关 键 词：Fretting wear Mixed fretting regime Zr alloy tube High temperature pressurized water Microstructure 

分 类 号：TG146.15[一般工业技术—材料科学与工程]