Effects of a high magnetic field on single-phase interface evolution,additional interfacial energy and nucleation undercooling in Al-based alloy  

作　　者：Lin Wang Zhipeng Long Long Hou Song Yan Baode Sun Xi Li 

机构地区：[1]Shanghai Key Lab of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong University, Shanghai, 200240, China [2]State Key Laboratory of Advanced Special Steels, Shanghai University, Shanghai, 200072, China

出　　处：《Journal of Materials Science & Technology》2023年第23期43-53,共11页材料科学技术（英文版）

基　　金：financed by the National Natural Science Foun-dation of China(Nos.51904183 and 52130204);the Inde-pendent Research and Development Project of State Key Labora-tory of Advanced Special Steel,Shanghai Key Laboratory of Ad-vanced Ferrometallurgy,Shanghai University(SKLASS 2021-Z07);the Science and Technology Commission of Shanghai Munic-ipality(Nos.19DZ2270200,20511107700).

摘　　要：The effects of a high magnetic field on the evolution of the single-phase interface and the liquid-solid interface energy in Al-Cu alloy were investigated experimentally.It is found that the application of the magnetic field has a significant promotion effect on the migration of liquid droplets,accelerating the formation of the single-phase interface.This should be attributed to the thermoelectric(TE)magnetic convection in the droplets which has enhanced the diffusion and increased the migration speed of liquid droplets.Further,the effect of the high magnetic field on the solid-liquid interface energy is analyzed by an improved grain boundary groove(GBG)method.The average solid-liquid interface energy of theα-Al/Al-Cu and Al2Cu/Al-Cu systems increases and decreases with the increase of the magnetic field,respectively.The above experiment results are well explained based on the formation and interaction of the magnetic dipole at the solid-liquid interface.Moreover,experimental results reveal that the magnetic-field-induced interface energy increases and decreases the nucleation undercooling of the Al-30wt.%Cu alloy and Al-35wt.%Cu alloy,respectively.By studying the effect of the magnetic-field-induced interface energy on the nucleation undercooling,the understanding of the interface energy-induced nucleation undercooling deepens.

关 键 词：High magnetic field Interface energy Nucleation undercooling Grain boundary groove 

分 类 号：TG146.16[一般工业技术—材料科学与工程]