Comparative study in vivo of the osseointegration of 3D-printed and plasma-coated titanium implants  

作　　者：Stanislav Bondarenko Volodymyr Filipenko Nataliya Ashukina Valentyna Maltseva Gennadiy Ivanov Iurii Lazarenko Dmytro Sereda Ran Schwarzkopf 

机构地区：[1]Department of Joint Pathology,Sytenko Institute of Spine and Joint Pathology National Academy of Medical Sciences of Ukraine,Kharkiv 61024,Ukraine [2]Laboratory of Connective Tissue Morphology,Sytenko Institute of Spine and Joint Pathology National Academy of Medical Sciences of Ukraine,Kharkiv 61024,Ukraine [3]Experimental Pathology,Sytenko Institute of Spine and Joint Pathology National Academy of Medical Sciences of Ukraine,Kharkiv 61024,Ukraine [4]Department of Traumatology,Military medical clinical center of the Central region,Vinnytsia 21018,Ukraine [5]Department of Surgery,Odesa city hospital 11,Odesa 65006,Ukraine [6]Hospital for Joint Diseases,NYU Langone Orthopedic Hospital,NY 10003,United States

出　　处：《World Journal of Orthopedics》2023年第9期682-689,共8页世界骨科杂志（英文版）

摘　　要：BACKGROUND Total hip arthroplasty is a common surgical treatment for elderly patients with osteoporosis,particularly in postmenopausal women.In such cases,highly porous acetabular components are a favorable option in achieving osseointegration.However,further discussion is needed if use of such acetabular components is justified under the condition of normal bone mass.AIM To determine the features of osseointegration of two different types of titanium implants[3-dimensional(3D)-printed and plasma-coated titanium implants]in bone tissue of a distal metaphysis in a rat femur model.METHODS This study was performed on 20 white male laboratory rats weighing 300-350 g aged 6 mo.Rats were divided into two groups of 10 animals,which had two different types of implants were inserted into a hole defect(2×3 mm)in the distal metaphysis of the femur:GroupⅠ:3D-printed titanium implant(highly porous);GroupⅡ:Plasma-coated titanium implant.After 45 and 90 d following surgery,the rats were sacrificed,and their implanted femurs were extracted for histological examination.The relative perimeter(%)of bone trabeculae[bone-implant contact(BIC%)]and bone marrow surrounding the titanium implants was measured.RESULTS Trabecular bone tissue was formed on the 45th day after implantation around the implants regardless of their type.45 d after surgery,group I(3D-printed titanium implant)and groupⅡ(plasma-coated titanium implant)did not differ in BIC%(83.51±8.5 vs 84.12±1.73;P=0.838).After 90 d,the BIC%was higher in group I(87.04±6.99 vs 81.24±7.62;P=0.049),compared to groupⅡ.The relative perimeter of the bone marrow after 45 d did not differ between groups and was 16.49%±8.58%for groupⅠ,and 15.88%±1.73%for groupⅡ.Futhermore,after 90 d,in groupⅠthe relative perimeter of bone marrow was 1.4 times smaller(12.96±6.99 vs 18.76±7.62;P=0.049)compared to the relative perimeter of bone marrow in groupⅡ.CONCLUSION The use of a highly porous titanium implant,manufactured with 3D printing,for acetabular components provides increa

关 键 词：Rats Hip arthroplasty FEMUR POROSITY 3-dimensional printing Microscopy 