Effect of low basicity refining slag on evolution and removal of oxide inclusions in 55SiCrA spring steel  被引量:3

在线阅读下载全文

作  者:Chen Wang Wei Tang Jiang-shan Zhang Jun-xiong Huang Kun-rui Shen Jun Chen Qing Liu 

机构地区:[1]State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing,Beijing 100083,China [2]Xiangtan Branch,Hunan Valin Iron&Steel Co.,Ltd.,Xiangtan 411100,Hunan,China

出  处:《Journal of Iron and Steel Research International》2023年第9期1755-1768,共14页

基  金:This work was financially supported by the State Key Laboratory of Advanced Metallurgy Foundation(No.41621005);the Subject of Xiangtan Branch,Hunan Valin Iron&Steel Co.,Ltd.,China(No.2018386).

摘  要:The laboratory experiments,thermodynamic analysis,dynamic analysis,and industrial trials were carried out to investigate the influence of refining slag on the evolution and removal of oxide inclusions in 55SiCrA spring steel.The reduction in basicity and Al_(2)O_(3) content in refining slag can reduce the[Al]s content in the molten steel,which is conducive to the control of the low melting point of inclusions.However,the refining slag with excessively low basicity transfers the oxygen element to molten steel and increases the Al_(2)O_(3) content in inclusions,which is harmful to the control of inclusions.According to the chemical compositions of inclusions and refining slag in laboratory experiments,their physical parameters were calculated.The maximum separation ratio and the moving time of inclusions to reach the maximum separation ratio(t_(max))of inclusions under different laboratory experimental conditions were studied.The maximum separation ratio of inclusions is positively correlated with the overall wettability(coshIMS)among the slag,steel,and inclusions.The maximum separation ratio of inclusions obtained by laboratory experiments is between 85%and 91%.The t_(max) decreases with the decline in basicity and Al_(2)O_(3) content of refining slag,but excessively low basicity will increase the t_(max).The basicity of refining slag in the range of 0.88–0.97 and the content of Al_(2)O_(3) less than 6%is not only conducive to reducing the content of Al_(2)O_(3) and the melting point of inclusions but also beneficial to removing the inclusions to the slag.The slag system shows good metallurgical results in industrial trials.

关 键 词:Thermodynamic analysis Dynamic analysis Oxide inclusion Evolution mechanism Removal ratio Overall wettability 

分 类 号:TG14[一般工业技术—材料科学与工程]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象