不同循环加载路径下黄麻织物/聚乙烯复合材料的变形特性  

Deformation characteristics of jute fabric/polyethylene composite under different cyclic loading paths

作　　者：汪泽幸[1] 周衡书[1] 杨敏 谭冬宜[1] WANG Zexing;ZHOU Hengshu;YANG Min;TAN Dongyi(College of Textile and Fashion,Hunan Institute of Engineering,Xiangtan,Hunan411104,China)

机构地区：[1]湖南工程学院纺织服装学院,湖南湘潭411104

出　　处：《纺织学报》2023年第9期99-107,共9页Journal of Textile Research

基　　金：湖南省教育厅科学研究项目(20A111,20B135);湖南省重点研究计划项目(2020NK2028)。

摘　　要：为深入研究复杂受力条件下纤维增强热塑性复合材料的力学行为特性,采用热压法制备黄麻织物/聚乙烯复合材料,分别对其在循环加载、逐级递增循环加载以及逐级递减循环加载路径下的变形特性进行了实验研究,分析了累积应变、各次循环应变以及应变回复系数的变化规律,并探讨了变形机制。结果表明:黄麻织物/聚乙烯复合材料的变形特性不仅受循环峰值应力的影响,同时还与循环加载路径密切相关;在分别循环加载和逐级递增循环加载路径下,该热塑性复合材料在各级加载阶段均表现出循环软化特性;在逐级递减循环加载路径下,复合材料在首级加载阶段亦表现出循环软化特性,但在后续加载阶段均表现出循环硬化特性。Objective Owning to the advantages in terms of low-density,low-cost,recyclability,and excellent mechanical properties,the natural fiber reinforced thermoplastic composites have broad application prospects in fields such as transportation and construction.However,natural fiber reinforced thermoplastic composites are still limited in engineering design and application,partly due to a lack of in-depth and comprehensive understanding of its mechanical properties and failure mechanisms under complex loading conditions.Therefore,the paper proposed to investigate the influence of cyclic loading paths on the deformation characteristics and mechanism of jute fabric/polyethylene composites.Method Jute fabric/polyethylene composite prepared by hot press method based on jute woven fabric as reinforcement and polyethylene film as matrix,the mechanical properties of the composite were tested under cyclic loading paths of constant-amplitude cyclic loading,stepwise increasing cyclic loading and decreasing cyclic loading.The accumulated strain,strain of each cycle and strain recovery factor were analyzed,and the deformation mechanism was also discussed.Results The jute fabric/polyethylene composite exhibited cyclic softening characteristic at all loading stages under constant-amplitude cyclic loading,and stepwise increasing cyclic loading and in first loading stage under stepwise decreasing cyclic loading led to cyclic hardening in the subsequent loading stages under stepwise decreasing cyclic loading(Fig.3).Under constant-amplitude cyclic loading and stepwise increasing cyclic loading,the jute fabric/polyethylene composite demonstrated similar deformation mechanism;and with the increase of cyclic peak stress and cycle number,the accumulative strain(accumulative maximum and residual strain)of each loading stage was increase(Fig.5),and the loading strain,elastic strain and residual strain of each loading stage were decrease(Fig.6).Under stepwise decreasing cyclic loading,the variation of accumulative strain,loading strain,elastic

关 键 词：黄麻织物 聚乙烯 热塑性复合材料 循环加载 加载路径 变形特性 

分 类 号：TS101.923[轻工技术与工程—纺织工程] TB332[轻工技术与工程—纺织科学与工程]