Investigation of Particle Breakdown in the Production of Composite Magnesium Chloride and Zeolite Based Thermochemical Energy Storage Materials  

作　　者：Louis F.Marie Karina Sałek Tadhg S.O’Donovan 

机构地区：[1]HeriotWatt University,Institute of Mechanical,Process and Energy Engineering,Edinburgh,UK

出　　处：《Energy Engineering》2023年第10期2193-2209,共17页能源工程（英文）

基　　金：funded by the UKRI DTP Scholarship:EP/R513040/1.

摘　　要：Composite thermochemical energy storage(TCES)represents an exciting field of thermal energy storage which could address the issue of seasonal variance in renewable energy supply.However,there are open questions about their performance and the root cause of some observed phenomena.Some researchers have observed the breakdown of particles in their production phase,and in their use.This study seeks to investigate the underlying cause of this breakdown.SEM and EDX analysis have been conducted on MgCl2 impregnated 13X zeolite composites of differing diameters,as well as LiX zeolite.This was done in order to study the level of impregnation of salt into the zeolite matrix,as well as the effect this impregnation process has on the morphology of the zeolite.Analysis was conducted using ImageJ software to study the effect of the impregnation process on the diameter of the particles.It has been found that a by weight impregnation concentration of magnesium chloride of 11.90%for the LiX zeolite,and 7.59%and 5.26%for the large diameter 13X zeolite and the small diameter 13X zeolite respectively has been achieved.It has been found that the impregnation process significantly affects themorphology of 13X zeolite particles,causing large fissures to form,and eventually resulting in the previously found breakdown of these particles.It has been verified that a primary factor influencing the breakdown of the 13X zeolite particles is the efflorescence and sub-fluorescence phenomena,which leads to a build-up of crystals in the zeolite pores.It has also been found that prolonged impregnation times and the use of high concentration salt solutions in the soaking process can induce significant crystal growth which also leads to the breakdown of these particles.Results demonstrate that LiX zeolite is the optimum host matrix choice in these conditions.These results will allow for the design of more resilient composite TCES particles.

关 键 词：Composites thermochemical energy storage salt-in-porous-matrix zeolites seasonal storage 

分 类 号：O64[理学—物理化学]